Polyimides, process for the preparation thereof and polyimide resin compositions

ABSTRACT

In one aspect, the present invention relates to polyimides having excellent thermal resistance and process for preparing the same comprising carrying out condensation of 4,4&#39;-bis(3-aminophenoxy)biphenyl with pyromellitic dianhydride in the presence of a different diamine compound and optionally with a different tetracarboxylic acid dianhydride. 
     In a second aspect, the present invention relates to a heat resistant resin composition consisting essentially of an aromatic polyetherimide and a defined polyimide. 
     In a third aspect, the present invention relates to a polyimide resin composition comprised on a defined polyimide and a separate high-temperature engineering polymer. 
     In a fourth aspect, the present invention relates to a resin composition comprised of a defined polyimide and an aromatic polyamideimide.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of allowed application Ser. No. 07/608,727filed Nov. 5, 1990, now U.S. Pat. No. 5,288,843, which is a continuation-in-part of application Ser. No. 196,492, filed on May 20, 1988, application Ser. No. 199,918, filed on May 27, 1988, application Ser. No. 202,031, filed on June 3, 1988, and application Ser. No. 551,314, filed Jul. 12, 1990,which is a continuation of application Ser. No. 426,715, filed on October 26, 1989, all of these latter applications now abandoned.

BACKGROUND OF THE INVENTION

(i) Field of the Invention

In one aspect, the present invention relates to polyimides that exhibit excellent thermal resistance and processability, and to a process for preparing the polyimides. In this aspect, the invention relates to a process for preparing crystalline polyimides by controlling the rate of crystallization without varying the substantial crystallinity of the polyimides, to a process for preparing non-crystalline polyimides having outstanding processability and thermal resistance, and to the polyimides prepared by these processes.

In other aspects, the invention relates to polyimide resin compositions having advantageous properties, such as heat and chemical resistance, mechanical strength and moldability.

(ii) Description of the Related Art

Polyimides prepared by reacting tetracarboxylic dianhydride and a diamine compound exhibit excellent mechanical strength, dimensional stability, high thermal resistance, flame retardance and electrical insulation properties. Hence polyimides have conventionally been used in various fields such as electrical and electronic instruments, aerospace and aircraft equipment, and transport machinery. These types of polyimides are expected to be useful in applications in which thermal resistance is required. Thus, various types of polyimides having the above characteristics have been developed.

Some of the polyimides, however, do not exhibit definite glass transition temperatures, although they exhibit excellent heat resistance, and hence must be processed by such means as sinter molding to be useful for molding purposes. Other polyimides have low glass transition temperatures and are soluble in halogenated hydrocarbons, although they exhibit excellent processability, and hence are unsatisfactory in view of their thermal and solvent resistances.

In order to obtain polyimides having the above desired properties, crystalline polyimides have also been developed. For example, polyimides derived from 4,4'-bis(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride and p-phenylenediamine have a crystal structure (T. L. St. Clair et al, J. Polym. Sci., Polym. Chem. ed. 1977, vol. 15, No. 6, p. 1529) as do polyimides derived from 3,3',4,4'-benzophenonetetracarboxylic dianhydride and 1,3-bis[4'-(3-aminophenoxy)benzoyl]benzene, which have a semi-crystalline structure (P. M. Hergenrother et al, SAMPE Journal, July/August 1988, p. 13).

Although the above crystalline polyimides exhibit superior thermal resistance as compared to non-crystalline polyimides, their crystalline structure causes difficulty in processing and thus their applications are limited.

No process has previously been known which can improve the processability of crystalline polyimides without impairing their essential property, i.e., thermal resistance.

It has previously been found that polyimides obtained by condensation of 4,4'-bis(3-aminophenoxy)biphenyl with pyromellitic dianhydride, containing recurring structural units represented by the formula (VI): ##STR1## have a glass transition temperature (hereinafter referred to as Tg) of 260° C., a crystallization temperature (hereinafter referred to as Tc) of from 310° to 340° C. and a crystalline melting point (hereinafter referred to as Tm) of from 367° to 90° C., and that such polyimides are crystalline polyimides that can be melt-processed and exhibit excellent chemical resistance [Japanese patent Laid-Open No. 62-205124 (U.S. Pat. No. 4,847,349)].

The polyimide has a much higher Tg of 260° C. as compared with a Tg of 140° C. of polyetherether ketone (Trade Mark; VICTREX PEEK, a product of ICI), a crystalline engineering plastic and a Tg of 225° C. of aromatic polysulfone (Trade Mark; VICTREX PES, a product of ICI), a non-crystalline engineering plastic. Consequently, the above polyimide is an excellent engineering plastic material in view of its thermal resistance.

The above polyimide, however, has a high Tm of from 367° to 390° C. and must be molded at a high temperature of about 400° C., which temperature causes processing problems. Further improvement of processability has been required for the above polyimide.

When a crystalline resin and a non-crystalline resin having the same level of glass transition temperature are compared in view of engineering plastics having high thermal resistance, the crystalline resin is generally excellent in chemical resistance and mechanical properties such as elastic modulus whereas the non-crystalline resin is outstanding in processability. Thus, crystalline resins and non-crystalline resins, respectively, have both advantages and drawbacks.

In consideration of the above circumstances, engineering plastics having good processability, excellent chemical resistance, high elastic modulus and good thermal resistance can be obtained, when the substantially excellent thermal resistance of crystalline polyimides consisting of recurring structural units represented by the above formula (VI) is maintained and processability is improved; for example, when processability is improved under the non-crystalline state in the processing step and polyimides having excellent thermal resistance can be subsequently obtained by converting to the crystalline state after processing. The same effect can also be obtained, when processability is improved by holding the non-crystalline state during and after processing step and the non-crystalline polyimide thus obtained has high thermal resistance.

It is expected that an essentially crystalline polymer would improve processability and to extend utilization to various fields of applications if a method is developed for freely controlling the crystallization rate of the polymer.

Investigations on the rate of crystallization and the method for controlling the rate have never been carried out on the crystalline polyimide.

Other polyimides also have been difficult to process or have other disadvantages. For example, polyimide consisting of a polymer chain represented by the following formula: ##STR2## (Trade Mark; KAPTON and VESPEL, products of E. I. du Pont de Nemours and Co.) indicates no distinct glass transition temperature and has an excellent heat resistance. The polyimide, however, is difficult to process by hot molding.

An aromatic polyetherimide (Trade Mark; ULTEM, a product of General Electric Co.) has been known to be capable of improving the processability of conventional polyimide. The typical aromatic polyetherimide is represented by the following formula: ##STR3## In spite of imide linkages in the molecule similar to conventional polyimide, the polyetherimide can be fusion molded and is excellent in mechanical strength, flame retardance, electrical property and molding ability, thereby having a wide field of use. Said aromatic polyetherimide, however, has a low heat distortion temperature of about 200° C. as compared with that of conventional polyimide of 280° C. Accordingly, reduction of mechanical and abrasion properties at high temperatures has caused problems on the development of its application. In order to improve these disadvantages solid lubricants such as graphite, fluororesin, titanium oxide and molybdenum disulfide are added to the aromatic polyetherimide in combination with or separately from inorganic fillers such as glass fibers and carbon fibers. However, the addition of inorganic fillers leads to lower abrasion resistance and that of solid lubricants tends to cause a marked reduction in mechanical strength.

A method for the simultaneous use of aromatic polyetherimide and another resin such as aromatic polyamideimide has also been developed. Even in such a case, however, retention of mechanical strength, particularly impact and abrasion resistances has been still unsatisfactory.

Other polyimides have a repeating unit represented by the formula: ##STR4## where X indicates a direct bond or is a radical selected from the group consisting of divalent hydrocarbon radicals having carbon atoms of 1 to 10, isopropylidene hexafluoride radical, carbonyl, thio, and sulfonyl, and R is a tetravalent radical selected from the group consisting of aliphatic radicals having at least 2 carbon atoms, alicyclic radicals, monocyclic aromatic radicals and fused polycyclic aromatic radicals, and polycyclic aromatic radicals including aromatic radicals interconnected directly or through a cross-linkage as for example, disclosed in Japanese Laid-Open Patent Nos. 143478/1986, 68817/1987, 86021/1987, and 50372/1987, and in Japanese Patent Application Nos. 076475/1986 and 274206/1986.

Within this definition can be obtained a thermoplastic polyimide having fluidity at high temperatures in addition to excellent mechanical, thermal and electrical properties which are substantial in polyimide. Compared to ordinary engineering polymers represented by polyethylene terephthalate, polybutylene terephthalate, polysulfone and polyphenylene sulfide, the polyimide is much superior in high-temperature resistance and other properties. On the other hand, the processing ability of the polyimide is still inferior to these polymers.

Further polyimides having excellent mechanical, thermal, electrical characteristics and solvent resistance and having heat resistance, have a repeating unit represented by the formula: ##STR5## where R is a tetravalent radical selected from the group consisting of aliphatic radicals having at least 2 carbon atoms, alicyclic radicals, monocyclic aromatic radicals and fused polycyclic aromatic radicals, and polycyclic aromatic radicals including aromatic radicals interconnected directly or through a cross-linkage (for example, Japanese Laid-Open Patent No. 50372/1987).

On the other hand, in the electronic field, there is required higher heat resistance with increasing integration in appliances and instruments.

Also, the aerospace material industry requires reduction in weight and improved strength of aircrafts with higher speed and larger amounts of transportation, reflecting the requirement for materials having high heat resistance and good strength compared with conventional thermoplastic resins.

SUMMARY OF THE INVENTION

Among its various aspects, the present invention overcomes the problems and disadvantages of the prior art by providing polyimides that exhibit excellent thermal resistance and processability.

It is an object of a first aspect of the invention to provide a polyimide having high thermal resistance and excellent processability.

It is a further object of the first aspect of the invention to provide a non-crystalline polyimide having excellent processability and high heat resistance.

It is an additional object of the first aspect of the invention to provide a process for preparing a crystalline polyimide by favorably and freely controlling the rate of crystallization in the processing of polyimide as a means for utilizing the essential high heat resistance while improving processability of the above crystalline polyimide.

It is an object of a second aspect of the invention to provide a heat resistant resin composition having mechanical strength, particularly impact and abrasion resistances at high temperatures, while maintaining excellent properties such as flame retardance, electrical properties, mechanical strength and moldability which are essential characteristics of aromatic polyetherimide.

It is an object of a third aspect of the invention to provide a molding resin composition containing polyimide which has a very excellent melt flowability without adverse effects on the essential properties of the polyimide.

It is an object of a fourth aspect of the invention to provide a polyimide resin composition having improved heat resistance and/or mechanical strength in addition to its intrinsic favorable properties.

Additional objects and advantages of the various aspects of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention. The objects and advantages of the invention will be realized and attained by means of the instrumentalities and combinations, particularly pointed out in the appended claims.

To achieve the objects in accordance with the purpose of the invention, as embodied and broadly described herein, a first aspect of the invention provides a process for preparing a polyimide comprising carrying out condensation of 4,4'-bis(3aminophenoxy)biphenyl of the formula (I): ##STR6## with a pyromellitic dianhydride of the formula (II): ##STR7## in the presence of at least one diamine compound selected from a defined list and optionally with a further tetracarboxylic acid dianhydride represented by the formula (IV) ##STR8## wherein R₂ is a tetravalent group selected from the group consisting of an aliphatic group, an alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group and a polycyclic aromatic group combined with a direct bond or via a bridge member.

Applicants have found that the essentially crystalline polyimide can be obtained in the form of noncrystalline polyimide by the process of the first aspect of the invention.

By the process of the first aspect of the invention, the rate of crystallization can be controlled, and processability can be improved without impairing the essential thermal resistance of the polyimide and without an adverse effect on the essential characteristics of the polyimide.

The polyimides prepared by the process of the first aspect of the invention exhibit excellent thermal resistance and processability and are useful in numerous applications such as molded articles and heat resistant films.

The accompanying drawings, which are incorporated in and constitute a part of this application, illustrate several exemplary embodiments of the first aspect of the invention and together with the description, serve to explain the principles of this aspect of the invention.

In a second aspect, the present invention relates to a resin composition consisting essentially of 95-5 wt. % of aromatic polyetherimide and 5-95 wt. % of a polyimide composed of recurring units represented by the formula ##STR9## wherein X is a direct bond or --S--, and Y is a tetravalent group selected from the group consisting of an aliphatic group having at least two carbon atoms, alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group and a polycyclic aromatic group where aromatic groups are connected to each other with a direct bond or via a bridge member.

In a third aspect, the present invention relates to a polyimide resin composition comprised of 99.9 to 50% by weight of polyimide which has recurring units of the formula: ##STR10## wherein Z is a direct bond, thio radical or a phenylene dicarbonyl radical where two carbonyl radicals are meta or para located on the benzene ring and Y is a tetravalent group selected from the group consisting of an aliphatic group having at least 2 carbon atoms, an alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group and a polycyclic aromatic group where aromatic groups are linked to one another directly or via a bridge member, and 0.1 to 50% by weight of high-temperature engineering polymer selected from the group consisting of polyphenylene sulfide, aromatic polysulfone and aromatic polyetherimide, and where said high temperature engineering polymer is polyphenylene sulfide or aromatic polysulfone when Z is the direct bond or thio radical.

In a fourth aspect, the present invention provides a resin composition which comprises 99.9 to 50% by weight of a polyimide having a recurring unit represented by the general formula: ##STR11## wherein Z is a direct bond or is ##STR12## and Y is a tetravalent group selected from the group consisting of an aliphatic group having at least 2 carbon atoms, an alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group, and a polycyclic aromatic group where the aromatic groups are connected directly or via a bridge member and 0.1 to 50% by weight of an aromatic polyamide imide.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates the relationship of crystallinity with time in a Geer oven at 300° C. in Example 9, 10 and Comparative Example 4.

FIG. 2 illustrates the relationship of crystallinity with time in a Geer oven at 300° C. in Examples 9, 11-13 and Comparative Example 4.

FIG. 3 illustrates the molding stability of the polyimide obtained in Example 15 and Example 20.

The molding stability was compared by changing the dwell time of the polyimide in the cylinder of a flow tester at a cylinder temperature of 420° C. and under a pressure of 100 kg/cm².

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Reference will now be made in detail to the present preferred embodiments of the various aspects of the invention.

In the process of the first aspect of the invention, the diamine compound and the tetracarboxylic acid dianhydride are preferably employed in an amount of from about 1 to about 100% by mole of 4,4'-bis(3-aminophenoxy)biphenyl and/or pyromellitic dianhydride. More preferably, the diamine compound and/or tetracarboxylic acid dianhydride are each employed in an amount of from about 1 to about 30% by mole. In such amounts, the rate of crystallization can be reduced to a desired level corresponding to the amount used and a crystalline polyimide can still be obtained. The polyimide powder thus obtained has improved processability due to its non-crystalline structure and can also be converted to a crystalline structure in the processing step to provide molded articles of polyimide having excellent thermal resistance.

When employed in an amount of from about 30 to about 100% by mole, the crystallization rate becomes extremely slow and a polyimide of substantially crystalline structure cannot be formed under typical processing conditions. Consequently, the resulting polyimide has a non-crystalline structure.

The non-crystalline polyimide thus obtained has improved processability and almost no loss is found in the high thermal resistance which is an essential characteristic of crystalline polyimide.

Suitable diamine compounds used to prepare the polyimides of this aspect of the invention include the compounds of the formula (III):

    H.sub.2 N--R.sub.1 --NH.sub.2                              III

wherein R₁ is a divalent group selected from the group consisting of an aliphatic group, an alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group and polycyclic aromatic group combined with a member selected from the group consisting of a direct bond and a bridge member and said diamine compound is selected from at least one of m-aminobenzylamine and p-aminobenzylamine and ethylenediamine; 1,4-diaminocyclohexane; m-phenylenediamine, o-phenylenediamine and p-phenylenediamine; diaminonaphthalenes such as 2,6-diaminonaphthalene; 4,4'-diaminobiphenyl; 3,4'-diaminobiphenyl and 3,3'-diaminobiphenyl; and bis (3-aminophenyl)ether, (3aminophenyl) (4-aminophenyl) ether, bis (3-aminophenyl) sulfide, (3-aminophenyl) (4-aminophenyl) sulfide, bis (4-aminophenyl) sulfide, bis(3-aminophenyl) sulfoxide, (3-aminophenyl) (4aminophenyl) sulfoxide, bis(4-aminophenyl) sulfoxide, bis (3-aminophenyl) sulfone, (3-aminophenyl)(4-aminophenyl) sulfone, bis(4-aminophenyl) sulfone, 3,3'-diaminobenzophenone, 3,4'-diaminobenzophenone, 4,4'-diaminobenzophenone, 3,3'-diaminodiphenylmethane, 3,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylmethane, bis[4-(4-aminophenoxy)phenyl]methane, 1,1bis[4-(4-aminophenoxy)phenyl]ethane, 1,2-bis[4-(4aminophenoxy)phenyl]ethane, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]butane, 2,2-bis[4-(4-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 1,3-bis(3aminophenoxy)benzene, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(3-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, bis[4-(4-aminophenoxy)phenyl]ketone, bis[4-(4-aminophenoxy)phenyl]sulfide, bis[4-(4-aminophenoxy)phenyl]sulfoxide, bis[4(4-aminophenoxy)phenyl]sulfone, bis[4-(4-aminophenoxy)phenyl]ether, 1,4-bis[4-(3-aminophenoxy)benzoyl]benzene, 1,3-bis[4-(3-aminophenoxy)benzoyl]benzene, 4,4'-bis[3-(4-aminophenoxy)-benzoyl]diphenyl ether, 4,4'-bis[3-(3-aminophenoxy)benzoyl]diphenyl ether, 4,4'bis[4-(4-amino-α,α-dimethylbenzyl)phenoxy]-benzophenone, 4,4' bis[4-(4-amino-α,α-dimethylbenzyl)phenoxy]-diphenyl sulfone and bis[4-{4-(4-aminophenoxy)phenoxy}phenyl]sulfone. The above compounds may be used singly or in combination. It will be noted that the diamine compound used in this aspect of the invention does not include 4,4'-bis(3-aminophenoxy)biphenyl.

The diamine compounds may be also at least one diamine compound selected from the group consisting of: ##STR13## wherein X₁ is a direct bond, O, CO, SO₂, SO, S, or CH₂ with the proviso that the diamine compound is not 4,4'diaminodiphenyl ether ##STR14## wherein X₂ is a direct bond, CO, SO₂, SO, S, ##STR15## wherein n is 1-4, and ##STR16## wherein X₂ is defined above.

Among the above diamine compounds exemplary preferred compounds include m-phenylenediamine, p-phenylenediamine, bis(3-aminophenyl) ether, (3-aminophenyl)(4-aminophenyl) ether, 1,3-bis(3-aminophenoxy)benzene, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(3-aminophenoxy)benzene and 1,4-bis(4-aminophenoxy)benzene.

Exemplary suitable tetracarboxylic acid dianhydrides of the formula (IV) which may be used to prepare the polyimides of this aspect of the invention include dianhydrides wherein R₂ is an aliphatic group, such as ethylenetetracarboxylic dianhydride and butanetetracarboxylic dianhydride; dianhydrides wherein R₂ is an alicyclic group, such as cyclopentanetetracarboxylic dianhydride; dianhydrides wherein R₂ is a monocyclic aromatic group, such as 1,2,3,4-benzenetetracarboxylic dianhydride; dianhydrides wherein R₂ is a fused polycyclic aromatic group, such as 2,3,6,7-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 3,4,9,10-perylenetetracarboxylic dianhydride, 2,3,6,7-anthracenetetracarboxylic dianhydride, and 1,2,7,8-phenanthrenetetracarboxylic dianhydride; dianhydrides wherein R₂ is a polycyclic aromatic group combined with a direct bond, such as 3,3',4,4'-biphenyltetracarboxylic dianhydride and 2,2',3,3'-biphenyltetracarboxylic dianhydride; and dianhydrides wherein R₂ is a polycyclic aromatic group combined via a bridge member, such as 3,3',4,4'-benzophenonetetracarboxylic dianhydride, 2,2',3,3'-benzophenonetetracarboxylic dianhydride, 2,2'-bis(3,4-dicarboxyphenyl)propane dianhydride, bis(3,4-dicarboxyphenyl) ether dianhydride, bis(2,3-dicarboxyphenyl) ether dianhydride, bis(3,4-dicarboxyphenyl) sulfone dianhydride, bis(2,3-dicarboxyphenyl) sulfone dianhydride, 2,2-bis(3,4-dicarboxyphenyl)-1,1,1,3,3,3-hexafluoropropane dianhydride, 2,2-bis(3,4-dicarboxyphenyl)1,1,1,3,3,3-hexachloropropane dianhydride, 1,1-bis(2,3-dicarboxyphenyl)ethane dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis(3,4-dicarboxyphenyl)methane dianhydride, 4,4'-(p-phenylenedioxy)diphthalic dianhydride and 4,4'-(m-phenylenedioxy)diphthalic dianhydride. The dianhydride compound may be used singly or in combination. Numerous tetracarboxylic acid dianhydrides may be used except pyromellitic dianhydride.

Among the above tetracarboxylic acid dianhydrides of the formula (IV), the compounds wherein R₂ is a polycyclic aromatic group combined with a direct bond or via a bridge member are preferably used. Exemplary preferred compounds include 3,3',4,4'-benzophenonetetracarboxylic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, bis(3,4-dicarboxyphenyl)ether dianhydride and 4,4'-(p-phenylenedioxy)diphthalic dianhydride. More preferably, 3,3',4,4'-biphenyltetracarboxylic dianhydride is employed.

The diamine compound and optionally the tetracarboxylic acid dianhydride of the formula (IV) are incorporated into the reaction system as auxiliary materials in the process of the first aspect of this invention. Reaction of the main materials in the presence of these auxiliary materials forms several kinds of imide units which are derived from the diamine ingredient containing 4,4'-bis(3-aminophenoxy)biphenyl and the diamine compound and the dianhydride ingredient containing pyromellitic dianhydride and the tetracarboxylic acid dianhydride of the formula (IV). These new types of units are thought to cut in the chain of essential recurring structural units of the formula (VI) derived from the main materials, i.e., 4,4'-bis(3-aminophenoxy)biphenyl and pyromellitic dianhydride, and to form a complex polymer chain of polyimide.

It is difficult to identify the structure of these polyimide linkages. In practice, however, crystalline polyimide or non-crystalline polyimide can be obtained by adjusting the amounts of the diamine compound and/or tetracarboxylic acid dianhydride for auxiliary use in the abovementioned range.

The diamine compound and the tetracarboxylic acid dianhydride represented by the formula (IV) may be used singly or as a mixture in a suitable proportion.

Preferably the diamine compound and tetracarboxylic acid dianhydride of the formula (IV) is employed in an amount of from about 1 to about 100% by mole of the main monomer, i.e., 4,4'-bis(3-aminophenoxy)biphenyl and/or pyromellitic dianhydride. Use in an amount less than about 1% by mole leads to a rapid rate of crystallization of the polyimide composed of the recurring structural units represented by the formula (VI). The resulting polyimide is rapidly converted to a crystalline polyimide and is unfavorable for improving processability. On the other hand, use in an amount exceeding 100% by mole results in an adverse effect on the excellent characteristics of the polyimide. Most preferably, the diamine compound and the tetracarboxylic acid dianhydride of the formula (IV) is employed in an amount of from about 5 to about 50% by mole of 4,4'-bis(3-aminophenoxy)biphenyl and/or pyromellitic dianhydride.

In the case where a non-crystalline polyimide is prepared from bis(4-aminophenyl)ether as the most preferable the diamine compound selected from the formula (III), bis(4-aminophenyl)ether is employed in an amount of from about 2 to about 30% by mole of 4,4'-bis(3-aminophenoxy)biphenyl.

A part of the bis(4-amino-phenoxy)ether may be replaced by other diamines without adverse effect on the beneficial properties of the polyimide. Exemplary suitable diamines to be used for the partial replacement have been set forth above.

A non-crystalline polyimide can be obtained by using the above amount. When used in an amount of about 30% by mole or less, the crystallization rate can be controlled to a desired level by selecting the treating conditions and a crystalline polyimide can also be prepared. In the same range of amount for use, it is also possible to prepare a non-crystalline polyimide and to convert the resultant non-crystalline polyimide to crystalline polyimide under selected processing conditions. In these cases, the amount of the diamine compound and tetracarboxylic acid dianhydride of the formula (IV) for auxiliary use is about 30% by mole or less, preferably from about 2 to about 30% by mole of the main monomer materials, i.e., 4,4'-bis(3-aminophenoxy)biphenyl and/or pyromellitic dianhydride. When an amount exceeding about 30% by mole is employed, it is difficult to give a substantially I0 crystalline polyimide. The use-of an amount in large excess of about 30% by mole can already provide a non-crystalline polyimide. Consequently, a crystalline polyimide can be arbitrarily obtained at a certain temperature at a desired rate of crystallization by selecting the amount of auxiliary monomer in the range of 30% by mole or less of 4,4'-bis(3-aminophenoxy)biphenyl and/or pyromellitic dianhydride, which means that processability can be improved and molded products having excellent thermal resistance can be simultaneously obtained.

In the process for preparing the polyimide of this invention, polyamic acid is prepared by reacting 4,4'-bis(3aminophenoxy)biphenyl with pyromellitic dianhydride in the presence of the diamine compound and/or a tetracarboxylic acid dianhydride of the formula (IV).

No particular restriction is imposed on the method of reaction. However, organic solvents are preferably used for the reaction. Exemplary suitable organic solvents include N,N-dimethylformamide, N,N-dimethylacetamide, N,N-diethylacetamide, N,N-dimethylmethoxyacetamide, N-methyl-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, N-methylcaprolactam, 1,2-dimethoxyethanebis(2-methoxyethyl)ether, 1,2-bis(2-methoxyethoxy) ethane, bis[2-(2-methoxyethoxy)ethyl]ether, tetrahydrofuran, 1,3-dioxane, 1,4-dioxane, pyridine, picoline, dimethyl sulfoxide, dimethyl sulfone, tetramethylurea, hexamethylphosphoramide, phenol, o-cresol, m-cresol, m-cresylic acid, p-cresol, p-chlorophenol and anisol. These organic solvents may be used singly or in combination.

A reaction temperature of about 250° C. or less is preferably employed, more preferably a temperature of about 50° C. or less is employed. No particular limitation is placed upon the pressure and the reaction can be satisfactorily carried out at atmospheric pressure. Reaction time is different depending upon the solvent and reaction temperature. A reaction time of from about 4 to about 24 hours is usually sufficient.

The polyamic acid thus obtained is further imidized by heating at from about 100° to about 400° C. or chemically imidized with an imidizing agent such as acetic anhydride, to obtain a polyimide having recurring units corresponding to the polyamic acid.

Alternatively, 4,4'-bis(3-aminophenoxy)biphenyl and pyromellitic dianhydride may be suspended or dissolved in an organic solvent together with the diamine compound and optionally the tetracarboxylic acid dianhydride of the above formula (IV). Then, the resulting mixture is heated to carry out formation of a polyamic acid precursor and simultaneous imidization. The polyimide can thus be prepared.

The above reactions are in some cases carried out in the presence of phthalic anhydride.

Preferably, phthalic anhydride is employed in an amount of from about 0.001 to about 1.0 mole per mole of the total diamine compounds used as the main and auxiliary materials. If employed in an amount less than about 0.001 mole, the phthalic anhydride does not provide thermal resistance of the polyimide at high temperatures, whereas an amount exceeding 1.0 mole lowers the mechanical strengths of the polyimide. Most preferably, the phthalic anhydride is employed in an amount of from about 0.001 to about 0.5 mole.

The reaction in the presence of phthalic anhydride may be carried out by any of the following methods.

(A) Reacting pyromellitic dianhydride with 4,4'-bis(3-aminophenoxy)biphenyl in the presence of the diamine compound and, when used, the tetracarboxylic acid dianhydride of the formula (IV) and successively continuing the reaction after adding phthalic anhydride.

(B) Carrying out the reaction of 4,4'-bis(3-aminophenoxy)biphenyl and the diamine compound with phthalic anhydride and successively continuing the reaction after adding pyromellitic dianhydride and, when used, the tetracarboxylic acid dianhydride of the formula (IV).

(C) Carrying out the reaction after simultaneously mixing pyromellitic dianhydride, 4,4'-bis(3-aminophenoxy)biphenyl, phthalic anhydride, the diamine compound and, when used, the tetracarboxylic acid dianhydride of the formula (IV).

The polyimide can also be prepared by suspending or dissolving 4,4'-bis(3-aminophenoxy)biphenyl, pyromellitic dianhydride, phthalic anhydride and the diamine compound and, when used, the tetracarboxylic acid dianhydride of the formula (IV) in an organic solvent and successively heating to carry out formation of a polyamic acid precursor and simultaneous imidization.

Films or powders of polyimides can be prepared by known methods.

The 4,4'-diaminodiphenyl ether is preferably employed an amount of from about 2 to about 30% by mole per mole of 4,4-bis(3-aminophenoxy)biphenyl. When employed in an amount less than about 2% by mole, the processability is about the same as that of a polyimide consisting of recurring structural units of the formula (VI), and hence no improvement is observed. On the other hand, when employed in an amount greater than about 30% by mole, thermoplasticity is drastically impaired, which is an essential characteristic of the polyimide consisting of the recurring structural units of the formula (VI).

More preferably, the 4,4'-diaminodiphenyl ether is employed in an amount of from about 5 to about 20% by mole of 4,4'-bis(3-aminophenoxy)biphenyl.

In this embodiment of the first aspect, the invention is carried out in the presence of phthalic anhydride. A part of the phthalic anhydride may be replaced by other dicarboxylic acid anhydrides so long as no adverse effect on the good properties of polyimide is observed.

Exemplary suitable dicarboxylic anhydrides for use in partial replacement include 2,3-benzophenonedicarboxylic anhydride, 3,4-benzophenonedicarboxylic anhydride, 2,3-dicarboxyphenylphenylether anhydride, 3,4-dicarboxyphenylphenylether anhydride, 2,3-biphenyldicarboxylic anhydride, 3,4-biphenyldicarboxylic anhydride, 2,3-dicarboxyphenylphenylsulfone anhydride, 3,4-dicarboxyphenylphenylsulfone anhydride, 2,3-dicarboxyphenylphenylsulfide anhydride, 3,4-dicarboxyphenylphenylsulfide anhydride, 1,2-naphthalenedicarboxylic anhydride, 2,3-naphthalenedicarboxylic anhydride, 1,8-naphthalenedicarboxylic anhydride, 1,2-anthracenedicarboxylic anhydride, 2,3-anthracenedicarboxylic anhydride and 1,9-anthracenedicarboxylic anhydride.

Preferably, phthalic anhydride is employed in an amount of from about 0.001 to about 1.0 mole per mole of the total diamine ingredients, i.e., the sum of 4,4'-bis(3-aminophenoxy)biphenyl of the formula (I) and 4,4'-diaminodiphenyl ether. When used in an amount less than about 0.001 mole, thermal stability at high temperatures can not be achieved, which is the object of this aspect of the invention. When used in an amount exceeding about 1.0 mole, a decrease in mechanical properties of the polyimide results. Most preferably, the phthalic anhydride is employed in an amount of from about 0.01 to about 0.5 mole per mole of the total diamine ingredients.

It is particularly preferred to carry out the above reaction in an organic solvent. Exemplary suitable organic solvents are set forth above. The organic solvent may be used singly or as a mixture.

The reaction may be carried out in the organic solvent by any of the following methods.

(A) Reacting pyromellitic dianhydride with 4,4'-bis(3-aminophenoxy)biphenyl and 4,4'-diaminodiphenyl ether, and successively continuing the reaction after adding phthalic anhydride.

(B) Reacting 4,4'-bis(3-aminophenoxy)biphenyl and 4,4'-diaminodiphenyl ether with phthalic anhydride, and successively continuing the reaction after adding pyromellitic dianhydride.

(C) Simultaneously reacting pyromellitic dianhydride, 4,4'-bis(3-aminophenoxy)biphenyl, 4,4'-diaminodiphenyl ether and phthalic anhydride.

The reaction temperature is preferably about 250° C. or less, more preferably about 50° C. or less. No particular limitation is placed on the reaction pressure and the reaction can be sufficiently carried out at atmospheric pressure. The reaction time differs depending upon the solvent and reaction temperature. A reaction time of from about 4 to about 24 hours is usually satisfactory.

The polyamic acid thus obtained is imidized by heating at from about 100° to about 400° C. or chemically imidized with an imidizing agent such as acetic anhydride to obtain a polyimide having recurring structural units corresponding to the polyamic acid.

The polyimide can also be obtained by suspending or dissolving 4,4'-bis(3-aminophenoxy)biphenyl, pyromellitic dianhydride, 4,4'-diaminodiphenyl ether and phthalic anhydride in an organic solvent and successively heating the resultant mixture to carry out formation of a polyamic acid precursor and simultaneous imidization.

The polyimide of the first aspect of this invention obtained by the above process contains two and more recurring structural units represented by the formula (V): ##STR17## wherein Q₁ and Q₂ are groups selected from the group consisting of an aliphatic group, an alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group and a polycyclic aromatic group combined with a direct bond or via a bridge member, Q₁ is a divalent group and Q₂ is a tetravalent group. The recurring structural units of the formula (V) contains about 50% by mole or more of the recurring structural units of the formula (VI): ##STR18## and from about 0.5 to about 50% by mole of at least one recurring structural unit of the formula (VII): ##STR19## wherein Q₂ is defined above and R₁ is a divalent group derived from at least one of said diamine compounds.

When the recurring structural units of the formula (VI) are present in an amount of about 50 to about 85% by mole and the amount of the recurring structural units of the formula (VII) is from about 15 to about 50% by mole, a non-crystalline polyimide is obtained.

When the recurring structural units of the formula (VI) are present in an amount of about 85% by mole or more, and the amount of the recurring structural units of the formula (VII) is from about 0.5 to about 15% by mole, a crystalline or non-crystalline polyimide can be obtained by controlling the rate of crystallization.

The constitution of the above recurring structural units in the polyimide obtained by the process of this invention cannot be identified as mentioned above. In practice, characteristic polyimide containing the above recurring structural units can be obtained.

Physical properties were measured on several kinds of non-crystalline polyimides obtained by the process of the first aspect of this invention. Ranges of the properties measured were Tg of 255° to 272° C., 5% weight loss temperature of 539° to 556° C. and heat distortion temperature of the molded specimen of 240° to 255° C. On the other hand, crystalline polyimides consisting of the recurring structural units of the formula (VI) exhibited corresponding properties of respectively 260° C., 545° C. and 245° C. These results illustrate that these polyimides are almost equal in heat resistance. The non-crystalline polyimides obtained in this aspect of the invention had a melt viscosity of 10800 to 40000 poises at 380° C. However, polyimides consisting of the recurring structural units of the formula (VI) did not flow at 380° C. The polyimide of this aspect of the invention has a melt flow initiation temperature of 322° to 328° C., whereas the crystalline polyimide of the formula (VI) has a considerably high initiation temperature of 74° C. The non-crystalline polyimides of the first aspect of the invention maintain high thermal resistance and have improved processability.

In the melt processing of polyimides obtained by the first aspect of the invention, a suitable amount of other thermoplastic resins may be blended depending upon the object for use, so long as there is no adverse effect on the objects of this aspect of the invention. Exemplary suitable thermoplastic resins include polyethylene, polypropylene, polycarbonate, polyallylate, polyamide, polysulfone, polyether sulfone, polyether ketone, polyphenylene sulfide, polyamideimide, polyetherimide and modified polyphenylene oxide.

Fillers which are used for common resin compositions may be added in an amount which do not cause any adverse effect on the objects of the first aspect of the invention. Exemplary suitable fillers include wear resistance improvers such as graphite, carborundum, silica powder, molybdenum disulfide and fluoro resins; reinforcing materials such as glass fibers, carbon fibers, boron fibers, silicon carbide fibers, carbon whiskers, asbestos, metallic fibers and ceramic fibers; flame retardance improvers such as antimony trioxide, magnesium carbonate and calcium carbonate; electrical property improvers such as clay and mica; tracking resistance improvers such as asbestos, silica and graphite; acid resistance improvers such as barium sulfate, silica and calcium metasilicate; thermal conductivity improvers such as iron powder, zinc powder, aluminum powder and copper powder; and other miscellaneous materials such as glass beads, glass balloons, talc, diatomaceous earth, alumina, silicate balloons, hydrated alumina, metal oxides and colorants.

The first aspect of the present invention provides non-crystalline polyimides having improved processability without decreasing the thermal resistance of essentially crystalline polyimides, having melt viscosities lower than that of conventionally known polyimide resins, and which have excellent melt flow-stability.

The polyimides of this aspect of the invention are useful in precision molded products and thermal resistant films and as a non-crystalline engineering plastic having outstanding thermal resistance.

The first aspect of the present invention also provides a method for preparing molded articles from non-crystalline to crystalline polyimide base resins by arbitrarily adjusting the rate of crystallization. Hence, this aspect of the invention can provide excellent polyimide resin having remarkably improved processability and thermal resistance, and is an industrially valuable invention.

In the second aspect of the present invention, the aromatic polyetherimide which is used is described in Polymer Preprint 24, (2), 312-313 (1983). The polyetherimide is a polymer consisting of ether and imide linkages as a required bonding unit and is substantially composed of recurring units which are represented by the following formula: ##STR20## wherein D is a trifunctional aromatic group where two functional groups out of three are connected with adjacent carbon atoms, both E and Ar₁ are residue of divalent aromatic groups. Representative examples of aromatic polyetherimide include the compounds represented by the following formulas: ##STR21##

Some of the above aromatic polyetherimide are commercially available from General Electric Co. with Trade Marks such as ULTEM-1000, ULTEM-4000 and ULTEM-6000.

The polyimide which is used in the second aspect of the invention is a compound consisting of recurring units represented by the formula: ##STR22## wherein X is a direct bond or --S--, and Y is a tetravalent group selected from the group consisting of an aliphatic group having at least 2 carbon atoms, an alicyclic group, monocyclic aromatic group, a fused polycyclic aromatic group and a polycyclic aromatic group where aromatic groups are connected to each other with a direct bond or via a bridge member.

As a diamine component of the polyimide, etherdiamine used is represented by the formula: ##STR23## wherein X is direct bond or --S--.

The etherdiamine is reacted with at least one tetracarboxylic acid dianhydride, and the resulting polyamic acid is subjected to dehydrating condensation to obtain polyimide.

Examples of the etherdiamine used in the second aspect of the invention include 4,4'-bis(3-aminophenoxy)biphenyl and bis[4-(3-aminophenoxy)phenyl]sulfide. The diamines may be used alone or as a mixture.

In addition, other diamines can be used in combination with the etherdiamine in a range which causes no adverse effect on the flowability of the molten polyimide. Diamines which may be used in admixture with etherdiamine include, for example, m-aminobenzylamine, p-aminobenzylamine, 3,3'-diaminodiphenyl ether, 3,4'-diaminodiphenyl ether, 4,4'-diaminodiphenylether, 3,3'-diaminodiphenyl sulfide, 3,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenyl sulfide, 3,3'-diaminodiphenyl sulfone, 3,4'-diamino-diphenyl sulfone, 4,4'-diaminodiphenyl sulfone, 3,3'-diaminobenzophenone, 3,4'-diaminobenzophenone, 4,4'-diaminobenzophenone, 1,3-bis(3-aminophenoxy)benzene, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(3-amino-phenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 2,2-bis[4-(4-aminophenoxy)phenyl propane, 4,4'-bis(4-aminophenoxy)biphenyl, 4,4'-bis(4aminophenoxy)ketone, bis[4-(4-aminophenoxy)phenyl]sulfide, bis[4-(4-aminophenoxy)phenyl]sulfone, bis[4-(3-aminophenoxy)phenyl]methane, 1,1-bis[4-(3-aminophenoxy)phenyl]-ethane, 1,2-bis[4-(3-aminophenoxy)phenyl]propane, 2,2-bis[4-(3-aminophenoxy)phenyl]propane, 2-[4-(3-aminophenoxy)phenyl]-2-[4-(3-aminophenoxy)-3-methylphenyl]propane, 2,2-bis[4-(3-aminophenoxy)-3-methylphenyl]propane, 2-[4-(3-aminophenoxy)phenyl]-2-[4-(3-aminophenoxy)-3,5-dimethylphenyl]propane, 2,2-bis4-(3-aminophenoxy)-3,5-dimethylphenyl]propane, 2,2-bis[4-(3-aminophenoxy)phenyl]butane, 2,2-bis[4-(3-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 4,4'-bis(3-aminophenoxy)biphenyl, 4,4'-bis(3-aminophenoxy)-3-methylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,3'-dimethylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,5-dimethylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,3',5,5'-tetramethylbiphenyl, bis[4-(3-aminophenoxy)phenyl]ketone, bis[4-(3-aminophenoxy)phenyl]sulfide and bis[4-(3aminophenoxy)phenyl]sulfone. These diamines are used in admixture with etherdiamine of the above formula in an amount of normally not more than 30 wt. %, and preferably not more than 5 wt. %.

The polyimide used in the second aspect of the present invention can be prepared by reacting the diamine with tetracarboxylic acid dianhydride in an organic solvent and followed by conducting dehydrating condensation.

The tetracarboxylic acid dianhydride used in this aspect of the invention has the following formula: ##STR24## where Y is the same as above. Representative examples of these tetracarboxylic acid dianhydrides include ethylenetetracarboxylic acid dianhydride, 1,2,3,4-butanetetracarboxylic acid dianhydride, cyclopentanetetracarboxylic acid dianhydride, pyromellitic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic acid dianhydride, 2,2',3,3'-benzophenonetetracarboxylic acid dianhydride, 3,3',4,4'-biphenyltetracarboxylic acid dianhydride, 2,2',3,3'-biphenyltetracarboxylic acid dianhydride, bis(3,4-dicarboxyphenyl)ether dianhydride, bis(3,4-dicarboxyphenyl) sulfone dianhydride, 1,1-bis(2,3-dicarboxyphenyl)ethane dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis(3,4-dicarboxyphenyl)methane dianhydride, 2,3,6,7-naphthalenetetracarboxylic acid dianhydride, 1,4,5,8-naphthalenetetracarboxylic acid dianhydride, 1,2,5,6-naphthalenetetracarboxylic acid dianhydride, 1,2,3,4-benzenetetracarboxylic acid dianhydride, 3,4,9,10-perylenetetracarboxylic acid dianhydride, 2,3,6,7-anthracenetetracarboxylic acid dianhydride, 1,2,7,8-phenanthrenetetracarboxylic acid dianhydride, 4,4'-(p-phenylenedioxy)diphthalic acid dianhydride and 4,4'-(m-phenylenedioxy)diphthalic acid dianhydride. Among these acid dianhydrides, pyromellitic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic acid dianhydride, 3,3',4,4'-biphenyltetracarboxylic acid dianhydride and 2,2-bis (3,4-dicarboxyphenyl)-1,1,1,3,3,3-hexafluoropropane dianhydride are particularly preferred.

The tetracarboxylic acid dianhydrides can be used alone or as a mixture of two or more.

The heat resistant resin composition of the second aspect of the invention consists essentially of 95-5 wt. % of aromatic polyetherimide and 5-95 wt. % of polyimide. A preferred composition consists of 90-10 wt. % of aromatic polyetherimide and 10-90 wt. % of polyimide. A more preferred composition consists of 80-20 wt. % of aromatic polyetherimide and 20-80 wt. % of polyimide. When the content of aromatic polyetherimide or polyimide is above 95 wt. % or below 5 wt. %, the composition of this aspect of the invention cannot provide a combination of excellent characteristics such as flowability, mechanical strength and particularly impact and abrasion resistances. That is, the second aspect of the present invention provides the essential flowability of aromatic polyetherimide with good mechanical strength and abrasion resistance of polyimide.

The composition of the second aspect of the invention may contain fillers used in known resin compositions in an amount which has no adverse effect on the object of this aspect of the invention. The fillers include abrasion resistance improvers such graphite, carborundum, silica powder, molybdenum disulfide and fluororesin; reinforcing materials such as glass fibers, carbon fibers, boron fibers, silicon carbide fibers, carbon whiskers, asbestos and metal fibers; flame retardance improvers such as antimony trioxide, magnesium carbonate and calcium carbonate; electrical property improvers such as clay and mica; tracking resistance improvers such as asbestos, silica and graphite; acid resistance improvers such as barium sulfate, silica and calcium metasilicate; thermal conductivity improvers such as iron powder, zinc powder, aluminum powder and copper powder; and other miscellaneous additives such as glass beads, glass spheres, talc, diatomaceous earth, alumina, silicate balloons, hydrated alumina, metal oxides, coloring agents and materials which are stable above 300° C.

These raw materials are used by mixing in advance. The mixing may be carried out by feeding each raw material separately to fusion mixing equipment or by mixing these materials in a general purpose mixer such as Henschel mixer, ball mixer and ribbon blender prior to feeding the materials to the fusion mixer.

Any procedure used for known resin compositions may be selected. The temperature of the fusion mixer is normally 250°-400° C. and preferably 300°-380° C. Any molding process including compression molding, sinter molding, injection molding and extrusion molding may be employed. Injection molding and extrusion molding are recommended from the viewpoints of the formation of a uniformly fused blend and high productivity.

In the third aspect of the invention, the polyimide is derived from etherdiamine of the following formula: ##STR25## wherein Z is a direct bond, thio radical or a phenylene dicarbonyl radical where two carbonyl radicals are meta or para located on the benzene ring.

The etherdiamine is 4,4'-bis(3-aminophenoxy)biphenyl, bis[4-(3-aminophenoxy)phenyl] sulfide, 1,3-bis[4-(3-aminophenoxy)benzoyl]benzene or 1,4-bis[4-(3-aminophenoxy)benzoyl]benzene.

These etherdiamines have the following formulae respectively: ##STR26##

The etherdiamine is reacted with at least one tetracarboxylic acid dianhydride in an organic solvent.

The tetracarboxylic acid dianhydride used in the above reaction is an anhydride of the formula: ##STR27## where Y is a tetravalent group selected from the group consisting of an aliphatic group having at least two carbon atoms, alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group and a polycyclic aromatic group where aromatic groups are connected to each other with a direct bond or via a bridge member.

The tetracarboxylic acid dianhydride used in the method includes, for example, ethylenetetracarboxylic dianhydride, butanetetracarboxylic dianhydride, cyclopentanetetracarboxylic dianhydride, pyromellitic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic dianhydride, 2,2',3,3'-benzophenonetetracarboxylic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, 2,2',3,3'-biphenyltetracarboxylic dianhydride, 2,2-bis(3,4-dicarboxyphenyl)propane dianhydride, 2,2-bis(2,3-dicarboxyphenyl)propane dianhydride, bis(3,4-dicarboxyphenyl ether dianhydride, bis(3,4-dicarboxyphenyl)sulfone dianhydride, 1,1-bis-(2,3-dicarboxyphenyl)ethane dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis(3,4-dicarboxyphenyl)methane dianhydride, 4,4'-(p-phenylenedioxy)diphthalic dianhydride, 4,4'-(m-phenylenedioxy)diphthalic dianhydride, 2,3,6,7-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 1,2,3,4-benzenetetracarboxylic dianhydride, 3,4,9,10-perylenetetracarboxylic dianhydride, 2,3,6,7-anthracenetetracarboxylic dianhydride and 1,2,7,8-phenanthrenetetracarboxylic dianhydride and 2,2-bis (3,4-dicarboxyphenyl)-1,1,1,3,3,3-hexafluoropropane dianhydride.

Particularly preferred tetracarboxylic acid dianhydrides are pyromellitic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic dianhydride and bis(3,4-dicarboxyphenyl)ether.

The tetracarboxylic acid dianhydride can be used alone or in the mixtures of two or more.

The polyimide which is used in the composition of the third aspect of the invention is prepared by using the above stated etherdiamine as a raw material. In order to obtain the composition of this aspect of the invention, other diamines can also be used in combination with the etherdiamine within the range which has no adverse effect on the good properties of the polyimide.

Examples of the diamines which may be used in admixture with the etherdiamine include, m-phenylenediamine, o-phenylenediamine, p-phenylenediamine, m-aminobenzylamine, p-aminobenzylamine, bis(3-aminophenyl)ether, (3-aminophenyl) (4-aminophenyl)ether, bis(4-aminophenyl)ether, bis(3-aminophenyl)sulfide, (3-aminophenyl) (4-aminophenyl)sulfide, bis(4-aminophenyl)sulfide, bis(3-aminophenyl)sulfoxide, (3-aminophenyl) (4-aminophenyl)sulfoxide, bis(4-aminophenyl)sulfoxide, bis(3-aminophenyl)sulfone, (3-aminophenyl) (4-aminophenyl)sulfone, bis(4-aminophenyl)sulfone, 3,3'-diaminobenzophenone, 3,4'diaminobenzophenone, 4,4'-diaminobenzophenone, bis[4-(4aminophenoxy)phenyl]methane, 1,1-bis[4-(4-aminophenoxy)phenylethane, 1,2-bis[4-(4-aminophenoxy)phenyl]ethane, 2,2-bis[4-(4aminophenoxy)phenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]butane, 2,2-bis(4-(4-aminophenoxy)phenyl-1,1,1,3,3,3-hexafluoropropane, 1,3-bis(3-aminophenoxy)benzene, 1,3-bis(4aminophenoxy)benzene, 1,4-bis(3-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 4,4'-bis(4-aminophenoxy) biphenyl, bis[4-(4-aminophenoxy)phenyl] ketone, bis[4-(4-aminophenoxy)phenyl] sulfide, bis[4-(4-aminophenoxy)phenyl]sulfoxide, bis[4-(4-aminophenoxy)phenyl]sulfone and bis[4-(4-aminophenoxy)-phenyl]ether.

The high temperature engineering polymer which is used in the third aspect of the present invention includes, for example, polyphenylene sulfide, aromatic polysulfone and aromatic polyetherimide. However, aromatic polyetherimide is excluded when Z is a direct bond or thio radical in the formula of the polyimide used in this aspect of the invention.

Polyphenylene sulfide is a resin having recurring units of the formula: ##STR28## The preparation process of the resin is disclosed, for example in U.S. Pat. No. 3,354,129 and Japanese Patent Publication TOKKOSHO 45-3368 (1970). The resin can be commercially available, for example, as RYTON (Trade Mark of Phillips Petroleum Co. in U.S.A.). According to the patent disclosure, polyphenylene sulfide is produced by reacting p-chlorobenzene with sodium sulfide monohydrate at 160°-250° C. under pressure in N-methylpyrrolidone solvent. Polyphenylene sulfide includes various grades such as from non-crosslinked to partially crosslinked polymers and polymers having different polymerization degrees. These grades can be easily produced by conducting a post-treatment process and are also available in the market. Therefore grades having suitable melt viscosity for the desired polymer blend can be optionally prepared or purchased in the market.

Aromatic polysulfone is a well known high temperature engineering polymer having a polymer chain represented by the formula: ##STR29## and described, for example, by V. J. Leslie et al, in CHEMITECH, July 1975, 426-432.

Representative examples of the recurring units constituting aromatic polysulfone of this aspect of the invention include: ##STR30##

Typical aromatic polysulfones include, for example, polysulfone consisting of recurring units represented by the formula: ##STR31## (Trade Mark; VICTREX PES, commercially available from Imperial Chemical Industries in Britain) and polysulfone consisting of recurring units represented by the formula: ##STR32## (Trade mark; UDEL POLYSULFONE, commercially available from Union Carbide Corp, in U.S.A.).

Grades of aromatic polysulfone having various polymerization degrees can be easily produced. Therefore grades having suitable melt viscosity for the desired polymer blend can be optionally selected.

Aromatic polyetherimide is a polymer having both ether and imide linkages as a required bonding unit and is substantially composed of recurring units of the following formula: ##STR33## wherein F is a trivalent aromatic radical where two valences out of three are connected with two adjacent carbon atoms, and Ar₂ and G are respectively a divalent monoaromatic group and a divalent polycyclic aromatic group connected with a bridge member.

This polyetherimide is also a well known high temperature engineering polymer and is described, for example, by Takekoshi et al in Polymer Preprint 24,(2), 312-313 (1983).

Suitable examples of recurring units constituting aromatic polyetherimide of this invention include: ##STR34##

Aromatic polyetherimide is commercially available from General Electric Co. in U.S.A. with the Trade Marks of ULTEM-1000, ULTEM-4000 and ULTEM-6000.

Aromatic polyetherimide particularly consisting of recurring units of the formula: ##STR35## is commercially available from General Electric Co. with the Trade Mark of ULTEM-1000.

Grades of aromatic polyetherimide having various polymerization degrees can be easily produced. Therefore grades having suitable melt viscosity for the desired polymer blend can be optionally selected.

The molding composition of resin in the third aspect of the invention is prepared so as to comprise the above mentioned polyimide in the range of 99.9 to 50% by weight and the high-temperature engineering polymer in the range of 0.1 to 50% by weight.

The resin of the third aspect of the invention based on polyimide/polyphenylene sulfide exhibits remarkably low melt viscosity in a high temperature region above 350° C. The good fluidization effect of polyphenylene sulfide can be found even in a small amount. The lower limit of the amount in the composition is 0.1% by weight. The preferred amount is not less than 0.5% by weight.

Polyphenylene sulfide is excellent in chemical resistance, water absorption and flame retardance among the high-temperature stable resins. It, however, is inferior particularly in elongation at break and impact resistance. Therefore, too much polyphenylene sulfide in the above composition is unfavorable because the essential mechanical strength of polyimide can not be maintained. The amount of polyphenylene sulfide in the composition has an upper limit and is preferably 50% by weight or less.

The resin composition of this aspect of the invention based on polyimide/aromatic polysulfone exhibits remarkably low melt viscosity in a high temperature region such as above 350° C. The good fluidization effect of aromatic polysulfone can be found even in a small amount. The lower limit of amount in the composition is 0.1% by weight. The preferred amount is not less than 0.5% by weight.

Aromatic polysulfone is excellent in mechanical strength at high temperatures among the high-temperature stable resins. It, however, is inferior to polyimide in mechanical strength, izod impact strength in particular. Therefore, too much aromatic polysulfone in the above composition is unfavorable because the essential mechanical strength of polyimide cannot be maintained. The amount of aromatic polysulfone in the composition has an upper limit and is preferably 50% by weight or less.

The resin composition of this aspect of the invention based on polyimide/aromatic polyetherimide exhibits remarkably low melt viscosity as compared with polyimide alone in a high temperature region, above 360° C. in particular. The effect can be found even in a small amount of aromatic polyetherimide. The lower limit in the composition is 0.1% by weight. The preferred amount is not less than 0.5% by weight.

Aromatic polyetherimide is excellent in mechanical strength at high temperatures among the high-temperature stable resins. It, however, is inferior to polyimide in mechanical strength, izod impact strength in particular. Therefore, too much aromatic polyetherimide is unfavorable because the essential mechanical strength of polyimide cannot be maintained.

Aromatic polyetherimide is easily soluble in halogenated hydrocarbons such as methylene chloride and chloroform as well as amide type solvents such as dimethyl acetamide and N-methyl-pyrrolidone. Therefore, too much aromatic polyetherimide in the composition is unfavorable because the essential solvent resistance of polyimide cannot be maintained.

For these reasons, the amount of aromatic polyetherimide has an upper limit in the composition and is preferably 50% by weight or less.

In the preparation of the composition in the third aspect of the invention, common known methods can be employed and, for example, the below described methods are preferred.

(1) Polyimide powder and high-temperature engineering polymer powder are pre-mixed to prepare a uniform mixture of powder by using a blender such as a mortar, Henschel mixer, drum blender, tumbler blender, ball mill or ribbon blender.

(2) Polyimide powder is previously dissolved or suspended in an organic solvent. High-temperature engineering polymer is added to the resulting solution or suspension and dispersed uniformly, followed by removing the solvent to give a powdered mixture.

(3) High-temperature engineering polymer is suspended in an organic solvent solution of polyamic acid which is the precursor of polyimide in this invention. The resultant suspension is imidized by heat treatment at 100°-400° C. or by chemical imidization with a conventional imidizing agent, followed by removing the solvent to give a powdered mixture.

The powdered resin composition of polyimide thus obtained can be used as is for various molding applications such as injection molding, compression molding, transfer molding and extrusion molding. A more preferred method is blending of fused resin prior to molding.

Fusion blending of polyimide and high-temperature engineering polymer in the forms of, respectively, powder and powder, pellet and pellet, or powder and pellet is also a simple and effective method.

Fusion blending can be carried out by using fusion blending equipment for usual rubber and plastics, for example, hot rolls, Banbury mixer, Brabender and extruder. The fusion temperature is set above the fusion temperature of the formulated system and below the initiation temperature of its decomposition. The temperature for blending polyimide with polyphenylene sulfide is normally in the range of 300°-420° C. and preferably in the range of 320°-400° C. The blending of polyimide with aromatic polysulfone or aromatic polyetherimide is carried out normally in the range of 280°-420° C. and preferably in the range of 300°-400° C.

As to the method of molding the resin composition in this aspect of the invention, injection and extrusion molding are suitable because these methods form a uniform blend of fused polymers and have a high productivity. Other processing methods such as transfer molding, compression molding and sinter molding may also be applied.

In addition, the resin composition of the third aspect of the invention may contain at least one solid lubricant such as molybdenum disulfide, graphite, boron nitride, lead monoxide and lead powder. The composition may also contain at least one reinforcing material such as glass fibers, carbon fibers, aromatic polyamide fibers, potassium titanate fibers and glass beads.

The resin composition of this aspect of the invention may also contain at least one commonly used additive within the range which has no adverse effect on the object of this invention. Such additives include, for example, antioxidants, heat stabilizers, ultraviolet ray absorbers, flame retardants, auxiliary flame retardants, antistatic agents, lubricants and coloring agents.

In the fourth aspect of the invention, the polyimides may be prepared by the process disclosed in the above-mentioned Japanese Laid-open Patent No. 143478/1986, which comprises reacting an ether diamine represented by the formula: ##STR36## where Z is a direct bond or is ##STR37##

Examples of diamines for use in the invention are 4,4'-bis(3-aminophenoxy)biphenyl; bis[4-(3-aminophenoxy)phenyl]sulfide; 1,4-bis[4-(3-aminophenoxy)benzoyl]benzene; and 1,3-bis[4-(3-aminophenoxy)benzoyl]benzene.

Any diamine other than the above-mentioned ether diamines, can be used in mixture therewith within such a range that good physical properties of the polyimide is not impaired. Examples of such a diamine are as follows: m-phenylenediamine, o-phenylenediamine, p-phenylenediamine, m-aminobenzylamine, p-aminobenzylamine, bis(3-aminophenyl)ether, (3-aminophenyl) (4-aminophenyl)ether, bis(4 -aminophenyl)ether, bis(3-aminophenyl)-sulfide, (3-aminophenyl) (4-aminophenyl)sulfide, bis(4-aminophenyl)sulfide, bis(4-aminophenyl)sulfide, bis(3-aminophenyl)sulfoxide, (3-aminophenyl) (4-aminophenyl)sulfoxide, bis(4aminophenyl)sulfoxide, bis(3-aminophenyl)sulfone, (3-aminophenyl) (4-aminophenyl)sulfone, bis(4-aminophenyl)sulfone, 3,3'-diaminobenzophenone, 3,4'-diaminobenzophenone, 4,4'-diaminobenzophenone, bis[4-(3-aminophenoxy)phenyl]methane, bis[4-(4-aminophenoxy)phenyl]methane, 1,1-bis[4-(3-aminophenoxy)phenyl]ethane, 1,1-bis[4-(4-aminophenoxy)phenyl]ethane, 1,2-bis[4-(3-aminophenoxy)phenyl]ethane, 1,2-bis[4-(4-aminophenoxy)phenyl]ethane, 2,2-bis[4-(3-aminophenoxy)phenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, 2,2-bis[4-(3-aminophenoxy)-phenyl]butane, 2,2-bis[4-(4-aminophenoxy)phenyl]butane, 2,2-bis[4-(3-aminophenoxy)phenyl] -1,1,1,3,3,3-hexafluoropropane, 2,2-bis[4-(4-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 1,3-bis(3-aminophenoxy)benzene, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(3-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 4,4'-bis(4-aminophenoxy)biphenyl, bis(4-(3-aminophenoxy)phenyl]ketone, bis[4-(4-aminophenoxy)phenyl]ketone, bis[4-(4-aminophenoxy)phenyl]sulfide, bis[4-(4-aminophenoxy)phenyl]sulfoxide, bis[4-(4-aminophenoxy)phenyl]sulfone, bis[4-(4-aminophenoxy)phenyl]sulfone, bis[4-(3-aminophenoxy)phenyl]ether, bis[4-(4-aminophenoxy)phenyl]ether, etc.

Tetracarboxylic dianhydrides for use in preparation of polyimides of the fourth aspect of the invention are represented by the formula: ##STR38## where Y is a tetravalent group selected from the group consisting of an aliphatic group having at least 2 carbon atoms, an alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group, and a polycyclic aromatic group where the aromatic groups are connected directly or via a bridge member and typical examples of these are ethylenetetracarboxylic acid dianhydride, butanetetracarboxylic acid dianhydride, cyclopentanetetracarboxylic acid dianhydride, pyromellitic dianhydride, 3,3,-4,4'-benzophenonetetracarboxylic acid dianhydride, 2,2',3,3'-benzophenonetetracarboxylic acid dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, 2,2',3,3'-biphenyltetracarboxylic acid dianhydride, 2,2-bis(3,4-dicarboxyphenyl)propane dianhydride, 2,2-bis(2,3-dicarboxyphenyl)propane dianhydride, bis(3,4-dicarboxyphenyl)ether dianhydride, bis(3,4-dicarboxyphenyl)sulfone dianhydride, 1,1-bis(3,4-dicarboxyphenyl)ethane dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis(3,4-dicarboxyphenyl)methane dianhydride, 4,4'-(p-phenylenedioxy)diphthalic acid dianhydride, 4,4'-(m-phenylenedioxy)diphthalic acid dianhydride, 2,3,6,7-naphthalenetetracarboxylic acid dianhydride, 1,4,5,8-naphthalenetetracarboxylic acid dianhydride, 1,2,5,6-naphthalenetetracarboxylic acid dianhydride, 1,2,3,4-benzenetetracarboxylic acid dianhydride, 3,4,9,10-perylenetetracarboxylic acid dianhydride, 2,3,6,7-anthracenetetracarboxylic acid dianhydride, and 1,2,7,8-phenanthrenetetracarboxylic acid dianhydride and 2,2-bis (3,4-dicarboxyphenyl)-1,1,1,3,3,3-hexafluoropropane dianhydride. These may be used alone or in combination of at least two.

Particularly preferred radicals in the Y defined above are tetravalent radicals represented in the formulas: ##STR39##

Aromatic polyamideimides suitable for use in the fourth aspect of the invention are polymers having as a repeating unit in the main chain a condensation product of imide and amide interconnected, which is represented by formula: ##STR40## where Ar₃ is a trivalent aromatic radical having at least one benzene ring, and J is a divalent organic radical.

Particularly preferred aromatic polyamideimides are the condensation polymers having a repeating unit represented by the following formulas: ##STR41##

An example of aromatic polyamideimide is commercially available under the trade name, TORLON® (Amoco Chemicals Corp., USA).

The resin composition to be molded according to the fourth aspect of the invention is composed of the abovementioned polyimide of 99.9 to 50% by weight, and the aromatic polyamideimide of 0.1 to 50% by weight, the sum amounting to 100% by weight.

The resin composition according to the fourth aspect of the invention consisting of the polyimide and the aromatic polyamideimide may be affected with even a small content of the latter with improvement in heat resistance and/or mechanical strength. The lower limit of the latter is 0.1% by weight, preferably 0.5% by weight.

Aromatic polyamideimides have very high melt viscosity compared with conventional thermoplastic resins, and therefore, too much aromatic polyamideimide in the resin composition produces unfavorable results, i.e., their moldability falls to an insufficient level, together with a drop in elongation at break. Thus the maximum content of aromatic polyamideimide is limited, and is preferably 50% by weight or less.

The resin composition according to the fourth aspect of the invention can usually be prepared by known methods, for example:

(1) A polyimide powder and an aromatic polyamideimide powder treated by mixing and/or kneading by means of a mortar, Henschel mixer, drum blender, tumbler blender, ball mill or ribbon blender to obtain the desired powder.

(2) A polyimide powder is dissolved or suspended in an organic solvent. To the solution or suspension, an aromatic polyamideimide is added, and made to be uniformly dispersed or dissolved. Then the solvent is removed to obtain the desired powder.

(3) An aromatic polyamideimide is dissolved or suspended in a solution of a polyamide acid in an organic solvent, which is the precursor of the polyimide according to this aspect of the invention, and then converted into an imide by heating to 100° to 400° C. or in the presence of a usual imidization agent. Then the solvent is removed to obtain the desired powder.

The thus-obtained powdery polyimide composition is subjected, preferably after melt-blending, to various processes, for example, injection, compression, transfer or extrusion molding. Especially, in the preparation of the resin composition, a simple and effective method is to melt-blend both components in the form of powders or pellets or one component of powders and the other component of pellets.

The melt-blending can be accomplished by usual means for blending rubbers or plastics, such as a hot roll, Banbury mixer, Brabender or extruder. The melting temperature may be set within the temperature range where the mixture can be caused to melt without thermal decomposition, usually 280° to 420° C., preferably 300° to 400° C.

For molding the resin composition of the fourth aspect of the invention, injection and extrusion moldings permitting formation of a uniform melt-blend with high productivity are preferred. Additionally, transfer, compression or sintering molding, or film extrusion may be applied.

The resin composition of the fourth aspect of the invention may contain as additives at least one solid lubricant selected from molybdenum disulfide, graphite, boron nitride, lead monoxide, lead powder, etc. and at least one reinforcing material selected from glass fibers, carbon fibers, aromatic polyamide fibers, silicon carbide fibers, potassium titanate fibers, glass beads, etc.

In addition, the resin composition may contain at least one additive selected from antioxidants, thermal stabilizers, ultraviolet ray absorbers, fire retardants, fire-retardant-activity enhancing agents, antistatic agents, lubricants, coloring agents, etc.

The invention will be further clarified by the following examples which are intended to be purely exemplary of the various aspects of the present invention wherein Examples 1-23 and Comparative Examples 1-9 relate to the first aspect of the invention, Examples 24-41 and Comparative Examples 10-14 relate to the second aspect of the invention, Examples 42-106 and Comparative Examples 15-39 relate to the third aspect of the invention, and Examples 107-131 and Comparative Examples 40-49 relate to the fourth aspect of the invention.

In the examples related to the first aspect of the invention, the properties in the examples and comparative examples were measured by the following methods.

Inherent Viscosity: After dissolving 0.50 g of polyimide powder in 100 ml of a solvent mixture of p-chlorophenol/phenol (9/1 weight ratio) by heating, the viscosity was measured at 35° C.

Tg, Tm and Tc: DSC (Shimadzu DT-40 series, DSC 41M) was used for the measurement.

Crystallinity: XRD (Rikadenki RAD-RVC Series, X-ray diffractometer) was used for the measurement.

Heat distortion temperature: ASTM, D-648I was used for the measurement.

Melt Viscosity: Shimadzu KOKA-model Flow Tester, CFT 500A was used under 100 kg load for the measurement.

Melt flow initiation temperature: Shimadzu KOKA-model Flow Tester, CFR 500A was used, and the melt flow initiation temperature was measured under 100 kg load.

5% Weight-Loss Temperature: Shimadzu DTA-TG was used in air for the measurement.

EXAMPLE 1

Into a reaction vessel equipped with a stirrer, reflux condenser, water separator and nitrogen inlet tube, 1.9872 kg (5.4 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.12 kg (0.6 mole) of 4,4'-diaminodiphenyl ether, 1.2426 kg (5.7 moles of pyromellitic dianhydride, 0.0888 kg (0.6 mole) of phthalic anhydride and 13.4 kg of cresylic acid were charged. The mixture obtained was heated to 145° C. with stirring in a nitrogen atmosphere while distilling off about 200 cc of water. The reaction was continued for 4 hours at 145° C.

After the reaction mixture was cooled to room temperature, about 7 kg of methyl ethyl ketone were charged and filtered to obtain polyimide as a yellow powder. The polyimide powder was washed with methyl ethyl ketone and dried at 180° C. for 24 hours under reduced pressure to obtain 3.16 kg of the product. The yield was 98%. The polyimide powder had an inherent viscosity of 0.50 dl/g and a glass transition temperature of 259° C. Tc and Tm were not observed. Melt viscosity was 14000 poise at 380° C. and 7000 poise at 400° C.

COMPARATIVE EXAMPLE 1

Into the same reaction vessel as described in Example 1, 2.208 kg (6 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 1.2426 kg (5.7 moles) of pyromellitic dianhydride, 0.0888 kg (0.6 mole) of phthalic anhydride and 13.4 kg of cresylic acid were charged. The same procedures as described in Example 1 were carried out and 3.27 kg of polyimide were obtained as yellow powder. The yield was 98.5%. The polyimide powder obtained had an inherent viscosity of 0.50 dl/g, a Tg of 260° C., a Tc of 332° C. and a Tm of 384° C. The polyimide had a melt viscosity of 7500 poise at 400° C. and did not flow at all at 380° C.

EXAMPLE 2

Into the same reaction vessel as described in Example 1, 2.208 kg (6 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 1.1183 kg (5.13 moles) of pyromellitic dianhydride, 0.1676 kg (0.57 mole) of 3,3',4,4'-biphenyltetracarboxylic dianhydride, 0.0888 kg (0.6 mole) of phthalic anhydride and 13.4 kg of cresylic acid were charged. The same procedures as described in Example 1 were carried out and 3.3 kg of yellow polyimide powder were obtained. The yield was 98%. The polyimide powder had an inherent viscosity of 0.48 dl/g and a Tg of 255° C. Tc and Tm were not observed. The melt viscosity was 16000 poise at 380° C.

EXAMPLE 3

Into the same reaction vessel as described in Example 1, 3.312 kg (9 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.2 kg (1 mole) of 4,4'-diaminodiphenyl ether and 17.58 kg of N,N-dimethylacetamide were charged. To the solution obtained, 2.126 kg (9.75 moles) of pyromellitic dianhydride were added by portions in a nitrogen atmosphere at room temperature with caution to inhibit temperature rise of the solution. The resulting mixture was stirred for about 20 hours at room temperature. A part of the polyamide acid solution thus obtained was cast on a glass plate and heated for each for 1 hour at 100° C., 200° C. and 300° C. to obtain a transparent light yellow polyimide film having a thickness of 25 μm. The polyimide film had a tensile strength of 16.5 kg/mm², elongation of 80% in accordance with ASTM D-882, and 5% weight loss temperature of 550° C. by DTA-TG.

EXAMPLES 4 TO 8 AND COMPARATIVE EXAMPLES 2 AND 3

The same reaction vessel as described in Example 1 and the procedures of Example 1 were repeated except that the diamines employed the amounts thereof were changed as illustrated in Table 1. The results are summarized in Table 1.

Tg, 5% weight loss temperature, melt viscosity, melt flow initiation temperature and heat distortion temperature of molded specimen are summarized in Table 2 for Examples 1, 2, 4 to 8 and Comparative Examples 1 and 2.

                                      TABLE 1                                      __________________________________________________________________________            Tetracarboxylic                                                                        Diamine ingredient           Inherent      Melt                 Example or                                                                            acid    4,4'-bis(3-aminoph-          viscosity     viscosity            Comparative                                                                           dianhydride                                                                            enoxy)biphenyl                                                                           Auxiliary diamine                                                                             Yield                                                                              (η)                                                                             Tg Tc Tm (poise/              Example                                                                               kg (mole)                                                                              kg (mole) kg (mole)      (%) (dl/g)                                                                              (°C.)                                                                      (°C.)                                                                      (°C.)                                                                      380°          __________________________________________________________________________                                                               C.)                  Ex. 4  Pyromellitic                                                                           1.9872 (5.4)                                                                             3,4'-diaminodiphenyl                                                                          98  0.481                                                                               260                                                                               No No 10800                       dianhydride       ether                                                        1.2496 (5.7)      0.12 (0.6)                                            Ex. 5  ↑   ↑ 3,3'-diaminodiphenyl                                                                          98  0.478                                                                               258                                                                               ↑                                                                           ↑                                                                           11600                                         0.12 (0.6)                                            Comp.  ↑ 0.8832 (2.4)                                                                             4,4'-diaminodiphenyl                                                                          gel-                                                                               Impossible to measure              Ex. 3                    0.72 (3.6)     ation                                  Ex. 6  ↑ 1.9872 (5.4)                                                                             bis[4- {4-(4-aminophenoxy)                                                                      97.5                                                                             0.508                                                                               258                                                                               No No 10800                                         phenoxy]} phenyl]sulfone                                                       0.3696 (0.6)                                          Ex. 7  ↑ 1.104 (3.0)                                                                              4,4'-bis[4-(4-amino-α , α-                                                        97  0.538                                                                               272                                                                               ↑                                                                           ↑                                                                           40000                                         dimethylbenzyl)phenoxy]diphe-                                                  nyl sulfone                                                                    1.336 (3.0)                                           Ex. 8  ↑ 1.9872 (5.4)                                                                             4,4'-bis[4-(4-amino-α, α-                                                         97  0.510                                                                               259                                                                               ↑                                                                           ↑                                                                           12300                                         dimethylbenzy)phenoxy]diphe-                                                   nyl sulfone                                                                    0.4008 (0.6)                                          Comp.  Pyromellitic                                                                           2.1896 (5.95)                                                                            4,4'-diaminodiphenyl                                                                          98  0.481                                                                               260                                                                               332                                                                               384                                                                               No flow              Ex. 2  dianhydride       ether                                                        1.2426 (5.7)      0.010 (0.05)                                          __________________________________________________________________________

                  TABLE 2                                                          ______________________________________                                         Example        5% weight Heat           Melt                                   or             loss      distortion                                                                             Melt   initiation                             Compara-       temper-   temper- viscosity                                                                             temper-                                tive    Tg     ature     ature   (poise/                                                                               ature                                  Example (°C.)                                                                          (°C.)                                                                             (°C.)                                                                           380° C.)                                                                       (°C.)                           ______________________________________                                         Ex. 1   259    555       244     14000  327                                    Ex. 2   255    553       240     16000  322                                    Ex. 4   260    556       245     10800  326                                    Ex. 5   258    550       243     11600  325                                    Ex. 6   258    546       243     10800  324                                    Ex. 7   272    539       255     40000  335                                    Ex. 8   259    540       244     12300  324                                    Comp.   260    545       245     No flow                                                                               374                                    Ex. 1                                                                          Comp.   260    546       246     ↑                                                                               372                                    Ex. 2                                                                          ______________________________________                                    

EXAMPLE 9

Into the same reaction vessel as described in Example 1, 3.312 kg (9.0 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.2 kg (1.0 mole) of 4,4'-diaminodiphenyl ether, 2,071 kg (9.5 moles) of pyromellitic dianhydride, 0.148 kg (1.0 mole) of phthalic anhydride and 21.58 kg of cresylic acid were charged. The mixture was heated to 145° C. with stirring in a nitrogen atmosphere while distilling out about 350 cc of water. The reaction was continued for 4 hours at 145° C. After the reaction mixture was cooled to room temperature, 10.8 kg of methyl ethyl ketone were charged and filtered. The yellow polyimide powder obtained was washed with methyl ethyl ketone and dried at 180° C. for 24 hours. The amount obtained was 5.26 kg (98% yield). The polyimide powder had an inherent viscosity of 0.50 dl/g and a glass transition temperature (Tg) of 260° C. The polyimide powder was extruded to 400° C. with a Takayasu model extruder having a diameter of 25 mm to obtain red brown transparent pellets. The pellets were further extruded to obtain a red brown transparent flexible film having a width of 50 mm and a thickness of 100 μm.

The rate of crystallization was measured on the polyimide film thus obtained by changing the standing time in a Geer oven at 300° C. The results are illustrated in FIG. 1. No crystallization was found at all until a standing time of 100 minutes in the Geer oven and 25% crystallinity was observed after 400 minutes.

COMPARATIVE EXAMPLE 4

Into the same reaction vessel as described in Example 1, 3.680 kg (10 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 2.071 kg (9.5 moles) of pyromellitic dianhydride, 0.148 kg (1.0 mole) of phthalic anhydride and 21.53 kg of cresylic acid were charged. The same procedures as described in Example 1 were carried out to obtain 5.46 kg of yellow polyimide powder. The yield was 98.5%. The polyimide powder had an inherent viscosity of 0.50 dl/g. An extruded film was prepared from the polyimide powder by the same procedures as described in Example 10 and the rate of crystallization was measured. Results are illustrated in FIG. 2.

Crystallization was initiated after standing for about 5 minutes in the Geer oven at 300° C. and 25% crystallinity was observed after 30 minutes.

EXAMPLE 10

Into the same reaction vessel as described in Example 1, 3.680 kg (10 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 1.864 kg (8.55 moles) of pyromellitic dianhydride, 0.279 kg (0.95 mole) of 3,3',4,4'-biphenyltetracarboxylic dianhydride, 0.148 kg (1.0 mole) of phthalic anhydride and 21.5 kg of cresylic acid were charged. The same procedures as described in Example 1 were carried out to obtain 5.51 kg of yellow polyimide powder. The yield was 98.2%. The polyimide powder had an inherent viscosity of 0.48 dl/g. An extruded film was prepared from the polyimide powder by the same procedures as described in Example 9 and the rate of crystallization was measured.

The results are illustrated in FIG. 1. Crystallization was not observed at all until 180 minutes after standing in the Geer oven at 300° C. and 25% crystallinity was observed after 500 minutes.

EXAMPLES 11 TO 13 AND COMPARATIVE EXAMPLE 5

The same reaction vessel as described in Example 1 was used and the procedures of Example 1 were repeated except that the amount of 4,4'-diaminodiphenyl ether was varied. The results are summarized in Table 3 and FIG. 2.

As understood from Table 3 and FIG. 2, addition of 4,4'-diaminodiphenyl ether in an amount of 25% by mole or less of 4,4'-bis(3-aminophenoxy)biphenyl can control the rate of crystallization. The control range is from 5 to 90 minutes in the initiation time of crystallization and from 300 to 3000 minutes in the time required for providing 25% crystallinity. Thus polyimides having a different rate of crystallization can be arbitrarily prepared.

                                      TABLE 3                                      __________________________________________________________________________                                                      Crystallization rate                                         Tetra-            of extruded film                     Diamine ingredient      carboxylic               Time to                Example or           (Diamine B/                                                                              acid      Inherent       25% crystall-          Comparative                                                                           Diamine A*.sup.1                                                                      Diamine B*.sup.2                                                                      Diamine A) × 100                                                                   dianhydride                                                                           yield                                                                             viscosity                                                                           Tg Initiation                                                                            inity                  Example                                                                               kg (mole)                                                                             kg (mole)                                                                             mole (%)  kg (mole)                                                                             (%)                                                                               (dl/g)                                                                              (°C.)                                                                      (min/300°                                                                      (min/300°                                                               C.)                    __________________________________________________________________________     Ex. 9  3.312  0.200  11.1      PMDA*.sup.3                                                                           98.0                                                                              0.50 258                                                                               100     400                          (9.0)  (1.0)            2.71 (9.5)                                      Ex. 11 3.496  0.100  5.3       ↑                                                                               98.5                                                                              0.51 258                                                                                50     100                          (9.5)  (1.0)                                                            Ex. 12 3.202  0.260  14.9      ↑                                                                               98.0                                                                              0.51 261                                                                               450    1000                          (8.7)  (1.3)                                                            Ex. 13 2.944  0.400  25.0      ↑                                                                               98.5                                                                              0.52 260                                                                               900    3000                          (8.0)  (2.0)                                                            Comp. Ex. 4                                                                           3.680  0      0         ↑                                                                               98.5                                                                              0.50 260                                                                                5      30                           (10.0)                                                                  Comp. Ex. 5                                                                           2.576  0.600  43.0      ↑                                                                               98.5                                                                              0.53 260                                                                               Do not crystallize                   (7.0)  (3.0)                              after 5000                    __________________________________________________________________________                                                      min.                           Note:                                                                          *.sup.1 : 4,4Bis(3-aminophenoxy)biphenyl                                       *.sup.2 : 4,4Diaminodiphenyl ether                                             *.sup.3 : Pyromellitic dianhydride                                       

EXAMPLE 14

The same reaction vessel as described in Example 1 was charged with 3.312 kg (9 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.2 kg (1.0 mole) of 4,4'-diaminodiphenyl ether and 31.5 kg of N-methyl-2-pyrrolidone. To the mixture obtained, 2.071 kg (9.5 moles) of pyromellitic dianhydride were added by portions at room temperature in a nitrogen atmosphere with caution to inhibit the temperature rise of the solution. Stirring was continued for 20 hours at room temperature. To the resulting polyamic acid solution, 0.444 kg (3 moles) of phthalic anhydride were added at room temperature in a nitrogen atmosphere and stirred for an additional hour. Successively 0.14 kg of τ-picoline and 0.408 kg (4 moles) of acetic anhydride were added dropwise to the solution. Yellow polyimide powder started to precipitate after an hour of completing addition of the dropwise addition. After stirring further for 10 hours at room temperature, the reaction mixture was filtered, washed by dispersing in methyl ethyl ketone, filtered again and dried at 180° C. for 24 hours. Polyimide powder thus obtained was 5.26 kg. The yield was 98%. The polyimide powder had a Tg of 258° C., an inherent viscosity of 0.50 dl/g and a melt viscosity of 7000 poise at 400° C.

EXAMPLE 15

Into the same reaction vessel as described in Example 1. 1.9872 kg (5.4 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.12 kg (0.6 mole) of 4,4'-diaminodiphenyl ether, 1.2426 kg (5.7 moles) of pyromellitic dianhydride, 0.0888 kg (0.6 mole) of phthalic anhydride and 13.4 kg of cresylic acid were charged. The mixture were heated to 145° C. with stirring in a nitrogen atmosphere while about 200 cc of water were distilled out. The reaction was further continued for 4 hours at 145° C. After cooling the reaction mixture to room temperature, about 7 kg of methyl ethyl ketone were added to the mixture and filtered. The resulting yellow powder was washed with methyl ethyl ketone and dried at 180° C. for 24 hours under reduced pressure to obtain 3.16 kg of polyimide powder. The yield was 98%. The polyimide had an inherent viscosity of 0.50 dl/g, a Tg of 259° C., and a melt viscosity of 14000 poise at 380° C. and 7000 poise at 400° C. Tc and Tm was not observed.

Molding stability of polyimide thus obtained was measured by varying residence time in the cylinder of the flow tester at 420° C. under pressure of 100 kg/cm². Results are illustrated in FIG. 3. Longer residence time in the cylinder has almost no effect on melt viscosity, which fact indicates good thermal stability.

COMPARATIVE EXAMPLE 6

Into the same reaction vessel as described in Example 1, 2.208 kg (6 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 1.2426 kg (5.7 moles) of pyromellitic dianhydride, 0.0888 kg (0.6 mole) of phthalic anhydride and 13.4 kg of cresylic acid were charged. The same procedures as described in Example 1 were carried out to obtain 3.27 kg of yellow polyimide powder. The yield was 98.5%. The polyimide powder had an inherent viscosity of 0.50 dl/g, a Tg of 260° C., a Tc of 332° C. and a melt viscosity of 7500 poise at 400° C. The polyimide powder exhibited no melt flow at 380° C.

EXAMPLES 16 TO 19 AND COMPARATIVE EXAMPLES 7 AND 8

The same reaction vessel as described in Example 1 was used, and the procedures of Example 14 were repeated except that the amount of 4,4'-diaminodiphenyl ether was varied as illustrated in Table 4. The results are summarized in Table 4.

                                      TABLE 4                                      __________________________________________________________________________            Diamine ingredient      Phthalic anhydride ingredient                   Example or           (Diamine B/     Phthalic anhydide                         Comparative                                                                           Diamine A*.sup.1                                                                      Diamine B*.sup.2                                                                      Diamine A) × 100                                                                   Amount                                                                               Diamine (A + B)                           Example                                                                               kg (mole)                                                                             kg (mole)                                                                             (mole %)  kg (mole)                                                                            (mole ratio)                              __________________________________________________________________________     Ex. 14 3.3120 0.200  11.1      0.444 0.3                                              (9.0)  (1.0)            (0.6)                                           Ex. 15 1.9872 0.120  11.1      0.0888                                                                               0.1                                              (5.4)  (0.6)            (0.6)                                           Ex. 16 2.0976 0.060  5.3       ↑                                                                              ↑                                          (5.7)  (0.3)                                                            Ex. 17 2.0424 0.900  8.1       ↑                                                                              ↑                                          (5.55)  (0.45)                                                          Ex. 18 1.9320 0.150  14.3      ↑                                                                              ↑                                          (5.25)  (0.75)                                                          Ex. 19 1.8768 0.180  17.6      ↑                                                                              ↑                                          (5.10) (0.9)                                                            Comp. Ex. 8                                                                           1.5456 0.360  42.9      ↑                                                                              ↑                                          (4.2)  (1.8)                                                            Comp. Ex. 6                                                                           2.2080 0      0         ↑                                                                              ↑                                          (6)                                                                     Comp. Ex. 7                                                                           2.1896 0.010  0.84      ↑                                                                              ↑                                          (5.95)  (0.05)                                                          __________________________________________________________________________                                  5% Weight                                         Example or       Inherent    loss                                              Comparative Yield                                                                               viscosity                                                                             Tg   temperature                                                                             Melt viscosity                           Example     (%)  (dl/g) (°C.)                                                                        (°C.)                                                                            (poise/380° C.)                   __________________________________________________________________________     Ex. 14      98.0 0.50   258  548      14000                                    Ex. 15      98.0 0.50   259  555      14000                                    Ex. 16      98.0 0.51   258  550      19000                                    Ex. 17      97.5 0.50   260  552      15800                                    Ex. 18      98.0 0.51   262  551      19300                                    Ex. 19      98.5 0.52   262  549      22300                                    Comp. Ex. 8 98.5 0.53   260  549      204000                                   Comp. Ex. 6 98.5 0.50   260  545      No flow                                  Comp. Ex. 7 98.0 0.48   260  550      No flow                                  __________________________________________________________________________      *.sup.1 : 4,4bis(3-aminophenoxy)-biphenyl                                      *.sup.2 : 4,4diaminodiphenylether                                        

EXAMPLE 20

The same procedures as described in Example 15 were carried out without using phthalic anhydride to obtain yellow polyimide powder. The polyimide powder had a Tg of 260° C. and an inherent viscosity of 0.50 dl/g.

Melt viscosity of the polyimide powder was measured by varying the residence time in the cylinder of the flow tester as carried out in Example 15. Results are illustrated in FIG. 3. Longer residence time led to higher viscosity. Thus thermal stability of the polyimide was inferior to that of Example 15.

EXAMPLE 21

The same reaction vessel as described in Example 1 was charged with 1.9872 kg (5.4 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.120 kg (0.06 mole) of bis(4-aminophenoxy) ether, 1.1183 kg (5.13 moles) of pyromellitic dianhydride, 0.1676 kg (.057 mole) of 3,3',4,4'-biphenyltetracarboxylic dianhydride and 13.4 kg of cresylic acid. The mixture was heated to 145° C. with stirring in a nitrogen atmosphere while about 200 cc of water were distilled out. The reaction was further continued for 4 hours at 145° C. After cooling the reaction mixture to room temperature, about 7 kg of methyl ethyl ketone were charged and filtered. The resulting yellow-powder was washed with methyl ethyl ketone and dried at 180° C. for 24 hours under reduced pressure. The polyimide powder obtained was 3.184 kg. The yield was 97.5%. The polyimide powder had an inherent viscosity of 0.49 dl/g, a Tg of 255° C. and a melt viscosity of 10000 poise at 380° C. Tc and Tm were not observed.

COMPARATIVE EXAMPLE 9

The same reaction vessel described in Example 1 was used to react the following reactants:

    ______________________________________                                         primary amine:      4.5 mole (75%)                                             4,4'diaminodiphenyl ether:                                                                         1.5 mole (25%) (33.3                                                           mole %/primary amine)                                      Pyromellitic dianhydride:                                                                          5.7 mole                                                   ______________________________________                                    

The resulting polyimide had the following properties:

    ______________________________________                                         Inherent viscosity:  0.491 dl/g                                                Tg (°C.):     261                                                       Tc (°C.):     No                                                        Tm (°C.):     No                                                        Crystallinity:       x                                                         HDT (°C.):    245                                                       5% Loss Temp. (°C.):                                                                         555                                                       Melt initiation Temp.:                                                                              327                                                       Melt viscosity:      42000 (380° C.)                                    ______________________________________                                    

EXAMPLE 22

Into the same reaction vessel as described in Example 1, 1.9872 kg (5.4 mole) of 4,4'-bis (3-aminophenoxy)biphenyl, 0.175 kg (0.6 moles) of 1,4-bis(4-aminophenoxy)benzene, 1.2426 kg (5.7 moles) of pyromellitic dianhydride, 0.0888 kg (0.6 moles) of phthalic anhydride and 13.4 kg of cresylic acid were charged. The same procedures as described in Example 1 were carried out and 3.2 kg of yellow polyimide powder were obtained. The yield was 98%. The polyimide powder had an inherent viscosity of 0.51 dl/g and a glass transition temperature of 258° C. Tc and Tm were not observed. Melt viscosity was 13,000 poise at 380° C.

EXAMPLE 23

Into the same reaction vessel as described in Example 1, 1.9872 kg (5.4 mole) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.300 kg (0.06 moles) of 1,4-bis[4-(3-aminophenoxy)benzoyl]benzene, 1.2426 kg (5.7 moles) of pyromellitic dianhydride, 0.0888 kg (0.6 moles) of phthalic anhydride and 13.4 kg of cresylic acid were charged.

The same procedures as described in Example 1 were carried out and 3.35 kg of yellow polyimide powder were obtained. The yield was 98.5%. The polyimide powder had an inherent viscosity of 0.50 dl/g and a glass transition temperature of 257° C. Tc and Tm were not observed. Melt viscosity was 12,100 poise at 380° C.

SYNTHESIS EXAMPLE 1 OF POLYIMIDE OF THE SECOND ASPECT OF THE INVENTION

A reaction vessel equipped with a stirrer, reflux condenser and nitrogen inlet tube was charged with 4.0 kg (10 moles) of 4,4'-bis(3-aminophenoxy)diphenyl sulfide and 34.8 kg of N,N-dimethylacetamide. To the mixture was added 2.14 kg (9.8 moles) of pyromellitic dianhydride in a nitrogen atmosphere in a manner so as to maintain the mixture at about room temperature and the mixture is stirred for about 20 hours at the room temperature.

To the polyamic acid solution obtained, 2.02 kg (20 moles) of triethylamine and 2.55 kg (25 moles) of acetic anhydride were added dropwise in a nitrogen atmosphere at the room temperature. The reaction mixture was stirred for about 20 hours to obtain a light yellow slurry. The slurry was filtered, washed with methanol, filtered again and dried at 180° C. for 8 hours under reduced pressure to obtain 5.64 kg (about 97.5% yield) of polyimide powder. The inherent viscosity of the polyimide powder was 0.85 dl/g.

The inherent viscosity was measured at 35° C. after dissolving 0.5 g of the polyimide powder in 100 ml of a solvent (a mixture of p-chlorophenol and phenol in a ratio of 90:10) at elevated temperatures.

EXAMPLES 24-27 AND COMPARATIVE EXAMPLES 10-11

The polyimide powder obtained in Synthesis Example 1 was dry blended with aromatic polyetherimide powder (Trade Mark; ULTEM 1000, a product of General Electric Co. in U.S.A.) in the ratio of Table 5 and pelletized by extruding at 370°-400° C. with a twin screw extruder. The pellets thus obtained was fed to an injection molding machine having a cylinder temperature of 360°-390° C., injection pressure of 1000 kg/cm² and mold temperature of 100°-150° C. The injection molded specimens were measured with respect to their mechanical and abrasion properties. The pellets obtained were fed to a Brabender type viscometer (Trade Mark; Laboplastomill, a product of Toyo Seiki Seisakusho Ltd.). Melt torque was measured under the conditions of 385° C. in temperature and 50 rpm in rotor revolution. Results obtained are illustrated in Table 5. Thermal properties were measured with a rectangular parallelopiped specimen having dimensions of 6×3×3 mm. The glass transition temperature Tg was measured with a thermo-mechanical analysis instrument (Trade Mark; TM-30, a product of Shimadzu Seisakusho Ltd.). Heat distortion temperature was examined with a load of 18.6 kg/cm² in accordance with ASTM D-648. As to the mechanical property, impact strength with a 1/8 inch notch was tested in accordance with ASTM D-256. As to the abrasion property, coefficient of abrasion was measured with a thrust abrader under such conditions that sliding velocity is 128 m/min and surface pressure is 0.78 kg/cm². The same testing methods as in Examples 24-27 were used in Examples 28-41 and Comparative Examples 10-11.

                                      TABLE 5                                      __________________________________________________________________________                                      Comparative                                              Example               example                                                  24    25    26   27   10   11                                       __________________________________________________________________________     Polymer (wt. %)                                                                Aromatic poly-                                                                            10    50    70   90   100  98                                       etherimide                                                                     (ULTEM 1000)                                                                   Polyimide  90    50    30   10   0    2                                        (Polymer                                                                       obtained in                                                                    Synthesis                                                                      Example 1)                                                                     Property                                                                       Glass transi-                                                                             235   232   227  220  215  217                                      tion tempera-                                                                  ture (°C.)                                                              Heat distor-                                                                              219   215   210  202  193  195                                      tion tempera-                                                                  ture (°C.)                                                              Izod impact                                                                               20.7  18.5  16.0 14.0 4.7  4.7                                      strength                                                                       (notched)                                                                      (kg · cm/cm)                                                          Abrasion co-                                                                   efficient                                                                      (× 10.sup.-8 cm.sup.3 /kg · m)                                   23° C.                                                                            72    80    88   98   201  200                                      250° C.                                                                            322   511   595  630  1785 1800                                     Friction co-                                                                   efficient                                                                       23° C.                                                                            0.25  0.25  0.25 0.25 0.25 0.25                                     250° C.                                                                            0.24  0.26  0.27 0.30 0.40<                                                                               0.40                                     Melt torque                                                                               130   115   88   80   78   77                                       (kg · cm)                                                                        -132  -118  -93  -83  -80  -80                                      __________________________________________________________________________

SYNTHESIS EXAMPLES 2-5

The same procedures as Synthesis Example 1 were carried out except that various diamines were used in place of 4,4'-bis(3-aminophenoxy)diphenyl sulfide, various tetracarboxylic acid dianhydrides were used in place of pyromellitic dianhydride, and the amounts of diamines, N,N-dimethylacetamide and tetracarboxylic acid dianhydrides were changed.

As a result, various kinds of polyimide powder were obtained. Table 6 illustrates synthetic conditions of polyimide and inherent viscosities of polyimide obtained under respective conditions of synthesis.

                                      TABLE 6                                      __________________________________________________________________________                                         Polyimide                                                    N,N-              inherent                                   Synthesis         Dimethyl                                                                             Tetracarboxylic acid                                                                       viscosity                                  example                                                                             Diamine      acetamide                                                                            dianhydride (dl/g)                                     __________________________________________________________________________     2    4,4'-Bis(3-aminophenoxy)                                                                    38.8 kg                                                                              3,3',4,4'-benzophenone-                                                                    0.62                                            biphenyl           tetracarboxylic acid                                        3.68 kg (10 moles) dianhydride                                                                    3.16 kg (9.85 moles)                                   3    4,4'-Bis(3-aminophenoxy)                                                                    33.0 kg                                                                              Pyromellitic                                                                               0.70                                            biphenyl           dianhydride                                                 3.68 kg (10 moles) 2.125 kg (9.75 moles)                                  4    4,4'-Bis(3-aminophenoxy)                                                                    33.7 kg                                                                              Pyromellitic                                                                               0.78                                            diphenyl sulfide   dianhydride                                                 3.8 kg (9 moles)   2.11 kg (9.7 moles)                                         4,4'-Diaminodiphenyl                                                           ether                                                                          0.202 kg (1 mole)                                                         5    4,4'-Bis(3-aminophenoxy)                                                                    32.3 kg                                                                              Pyromellitic                                                                               0.72                                            biphenyl           dianhydride                                                 3.5 kg (9.5 moles) 2.10 kg (9.65 moles)                                        4,4'-Diaminodiphenyl ether                                                     0.101 kg (0.5 mole)                                                       __________________________________________________________________________

EXAMPLES 28-38 AND COMPARATIVE EXAMPLES 12-14

The polyimide powder obtained in Synthesis examples 2-5 was kneaded with aromatic polyetherimide powder (Trade Mark; ULTEM 1000, a product of General Electric Co. in U.S.A.) by fusing in various mixing ratios to obtain uniformly blended pellets. The pellets obtained were molded in the same conditions as described in Example 23. Thermal, mechanical and abrasive properties were measured on the molded specimens and are illustrated in Tables 8-11 Besides the correspondence of polyimide used to examples and comparative examples is shown in Table 7.

                  TABLE 7                                                          ______________________________________                                                   Example     Comparative                                                                               Table                                         Polyimide No.         example No.                                                                               No.                                           ______________________________________                                         Synthesis 28-30       12          8                                            example 2                                                                      Synthesis 31-34       13          9                                            example 3                                                                      Synthesis 35-36       --         10                                            example 4                                                                      Synthesis 37-38       14         11                                            example 5                                                                      Synthesis 39-41       --         12                                            example 3                                                                      ______________________________________                                    

                  TABLE 8                                                          ______________________________________                                                                     Compar-                                                                        ative                                                        Example           example                                                      28      29       30       12                                         ______________________________________                                         Polymer (wt. %)                                                                Aromatic    50        70       90     97                                       polyetherimide                                                                 (ULTEM 1000)                                                                   Polyimide (Polymer                                                                         50        30       10     3                                        obtained in                                                                    Synthesis                                                                      Example 2)                                                                     Property                                                                       Glass transition                                                                           231       227      221    218                                      temperature (°C.)                                                       Heat distortion                                                                            214       210      204    199                                      temperature (°C.)                                                       Izod impact strength                                                                       15.0      13.5     11.2   5.0                                      (notched)                                                                      (kg · cm/cm)                                                          Abrasion Coefficient                                                           (× 10.sup.-8 cm.sup.3 /                                                  kg · m)                                                                23° C.                                                                             78        87       96     198                                      250° C.                                                                             499       587      600    1790                                     Friction coefficient                                                            23° C.                                                                             0.24      0.24     0.25   0.25                                     250° C.                                                                             0.24      0.26     0.31   0.40<                                    Melt torque 114       87       79     75                                       (kg · cm)                                                                         -118      -92      -83    -78                                      ______________________________________                                    

                                      TABLE 9                                      __________________________________________________________________________                                       Comparative                                              Example               example                                                  31    32    33   34   13                                           __________________________________________________________________________     Polymer (wt. %)                                                                Aromatic polyetherimide                                                                    10    50    70   90   98                                           (ULTEM 1000)                                                                   Polyimide (Polymer                                                                         90    50    30   10   2                                            obtained in Synthesis                                                          Example 3)                                                                     Property                                                                       Glass transition                                                                           255   253   249  236  219                                          temperature (°C.)                                                       Heat distortion                                                                            238   235   231  216  199                                          temperature (°C.)                                                       Izod impact strength                                                                       18.2  16.1  14.0 10.0 4.7                                          (notched) (kg · cm/cm)                                                Abrasion Coefficient                                                           (× 10.sup.-8 cm.sup.3 /kg · m)                                  23° C.                                                                              50    71    81   92   200                                          250° C.                                                                             302   490   570  820  1787                                         Friction coefficient                                                           23° C.                                                                              0.21  0.22  0.24 0.25 0.25                                         250° C.                                                                             0.21  0.24  0.25 0.29 0.40<                                        Melt torque 132   115   89   81   76                                           (kg · cm)                                                                         <135  -117  -91  -83  -78                                          __________________________________________________________________________

                  TABLE 10                                                         ______________________________________                                                         Example                                                                        35      36                                                     ______________________________________                                         Polymer (wt. %)                                                                Aromatic polyetherimide                                                                          10        90                                                 (ULTEM 1000)                                                                   Polyimide (Polymer                                                                               90        10                                                 obtained in Synthesis                                                          Example 4)                                                                     Property                                                                       Glass transition  285       247                                                temperature (°C.)                                                       Heat distortion   265       222                                                temperature (°C.)                                                       Izod impact strength                                                                             20        15                                                 (notched) (kg · cm/cm)                                                Abrasion Coefficient                                                           (× 10.sup.-8 cm.sup.3 /kg · m)                                  23° C.     68        96                                                 250° C.    329       615                                                Friction coefficient                                                           23° C.     0.24      0.24                                               250° C.    0.22      0.31                                               Melt torque       131       80                                                 (kg · cm)                                                                               -133      -84                                                ______________________________________                                    

                  TABLE 11                                                         ______________________________________                                                                   Comparative                                                      Example       example                                                          37      38        14                                               ______________________________________                                         Polymer (wt. %)                                                                Aromatic polyetherimide                                                                      25        90        98                                           (ULTEM 1000)                                                                   Polyimide (Polymer                                                                           75        10        2                                            obtained in Synthesis                                                          Example 5)                                                                     Property                                                                       Glass transition                                                                             290       255       220                                          temperature (°C.)                                                       Heat distortion                                                                              274       235       200                                          temperature (°C.)                                                       Izod impact strength                                                                         17        12        4.6                                          (notched) (kg · cm/cm)                                                Abrasion Coefficient                                                           (× 10.sup.-8 cm.sup.3 /kg · m)                                  23° C. 48        78        196                                          250° C.                                                                               390       592       1305                                         Friction coefficient                                                           23° C. 0.21      0.23      0.24                                         250° C.                                                                               0.22      0.27      0.40<                                        Melt torque   121       82        77                                           (kg · cm)                                                                           -127      -85       -80                                          ______________________________________                                    

EXAMPLES 39-41

The polyimide powder obtained in Synthesis example 3 was kneaded with aromatic polyetherimide powder (Trade Mark; ULTEM 6000, a product of General Electric Co. in U.S.A.) by fusing in various mixing ratios to obtain uniformly blended pellets. The pellets obtained were molded in the same conditions as described in Example 24. Thermal and mechanical properties were measured on the molded specimens and are illustrated in Table 12.

                  TABLE 12                                                         ______________________________________                                                       Example                                                                        39      40      41                                               ______________________________________                                         Polymer (wt. %)                                                                Aromatic polyetherimide                                                                        10        50      90                                           (ULTEM 6000)                                                                   Polyimide (Polymer                                                                             90        50      10                                           obtained in Synthesis                                                          Example 3)                                                                     Property                                                                       Glass transition                                                                               258       256     242                                          temperature (°C.)                                                       Heat distortion 238       236     221                                          temperature (°C.)                                                       Izod impact strength                                                                           18.3      17.0    12.0                                         (notched) (kg · cm/cm)                                                ______________________________________                                    

SYNTHESIS EXAMPLE 1 OF THE POLYIMIDE OF THE THIRD ASPECT OF THE INVENTION

A reaction vessel equipped with a stirrer, reflux condenser and nitrogen inlet tube was charged with 4.0 kg (10 moles) of bis[4-(3-aminophenoxy)phenyl] sulfide and 34.8 kg of N,N-dimethylacetamide. To the mixture was added 2.14 kg (9.8 moles) of pyromellitic dianhydride by portions in a nitrogen atmosphere at the room temperature and at a rate to avoid a large temperature rise of the solution and stirred for 20 hours at the room temperature.

To the resultant polyamic acid solution, 2.02 kg (20 moles) of triethylamine and 2.55 kg (25 moles) of acetic anhydride were added dropwise in nitrogen atmosphere at the room temperature and stirred for 20 hours at the room temperature to obtain a light yellow slurry. The slurry was filtered to obtain light yellow polyimide powder. The polyimide powder was formed into a sludge with methanol, filtered and dried at 180° C. for 8 hours under reduced pressure to obtain 5.63 kg (about 97.5% yield) of polyimide powder. The inherent viscosity of the polyimide powder was 0.85 dl/g. The inherent viscosity was measured at 35° C. after dissolving 0.5 g of the polyimide powder in 100 ml of a solvent (a mixture of p-chlorophenol and phenol in a ratio of 90:10 by weight) at elevated temperatures and cooling the resulting solution.

SYNTHESIS EXAMPLES 2-5

The same procedures as Synthesis Example 1 were carried out. However, raw materials were changed as follows. Various diamines were used in place of [4-(3-aminophenoxy)phenyl] sulfide and various tetracarboxylic acid dianhydrides were used in place of pyromellitic dianhydride. The amounts of diamines, N,N-dimethylacetamide and tetracarboxylic acid dianhydride were varied to obtain various polyimide powders. Table 13 illustrates conditions for the synthesis of the polyimide resins.

                                      TABLE 13                                     __________________________________________________________________________                            N,N-dimethyl                                                                          Tetracarboxylic acid                                                                             Inherent                       Synthesis                                                                           Diamine           acetimide                                                                             dianhydride       viscosity                      example                                                                             kg (mole)         kg (mole)                                                                             kg (mole)         (dl/g)                         __________________________________________________________________________     2    4,4'Bis(3-aminophenoxy)biphenyl                                                                  38.8 kg                                                                               3,3',4,4'-Benzophenonetetracarboxylic                                                            0.62                                3.68 kg (10 moles)       dianhydride                                                                    3.16 kg (9.85 moles)                             3    4,4'-Bis(3-aminophenoxy)biphenyl                                                                 33 kg  Pyromellitic dianhydride                                                                         0.70                                3.68 kg (10 moles)       2.125 kg (9.75 moles)                            4    Bis[4-(3-aminophenoxy)phenyl] sulfide                                                            33.7 kg                                                                               Pyromellitic dianhydride                                                                         0.78                                3.6 kg (9 moles)         2.11 kg (9.7 moles)                                   Bis(4-aminophenyl) ether                                                       0.202 kg (1 mole)                                                         5    4,4'-Bis(3-aminophenoxy)biphenyl                                                                 32.3 kg                                                                               Pyromellitic dianhydride                                                                         0.72                                3.5 kg (9.5 moles)       2.10 kg (9.65 moles)                                  Bis(4-aminophenyl) ether                                                       0.101 kg (0.5 mole)                                                       __________________________________________________________________________

SYNTHESIS EXAMPLE 6

A reaction vessel equipped with a stirrer, reflux condenser and nitrogen inlet tube was charged with 5 kg (10 moles) of 1,3-bis[4-(3-aminophenoxy)benzoyl]benzene and 40.5 kg of N,N-dimethylacetamide. The mixture was cooled to about 0° C. and 2.147 kg (9.85 moles) of pyromellitic dianhydride was added in five portions in a nitrogen atmosphere at a rate to avoid a large temperature rise of the solution. Then the temperature of the reaction mixture was raised to the room temperature and the mixture was stirred for 20 hours at the room temperature.

To the resultant polyamic acid solution, 2.02 kg (20 moles) of triethylamine and 2.55 kg (25 moles) of acetic anhydride were added dropwise in a nitrogen atmosphere at the room temperature and stirred for 20 hours at the room temperature to obtain a yellow slurry. The slurry was filtered to obtain light yellow polyimide powder. The polyimide powder was formed into a sludge with methanol, filtered and dried at 150° C. for 8 hours under reduced pressure to obtain 6.6 kg (about 97.5% yield) of polyimide as light yellow powder. The glass transition temperature Tg of the powder was 235° C. in accordance with DSC method.

Besides the inherent viscosity of the powder was 0.86 dl/g.

SYNTHESIS EXAMPLES 7-10

The same procedures as Synthesis example 6 were carried out by using various combinations of diamines and tetracarboxylic acid dianhydrides to obtain a variety of polyimides. Table 14 illustrates synthesis conditions, inherent viscosities and glass transition temperatures of the polyimide powders.

                                      TABLE 14                                     __________________________________________________________________________                               Tetracarboxylic acid                                                                             Inherent                           Synthesis                                                                           Diamine              dianhydride       viscosity                                                                           Tg                            example                                                                             kg (mole)            kg (mole)         (dl/g)                                                                              (°C.)                  __________________________________________________________________________     7    1,3-bis[4-(3-aminophenoxy)benzoyl]benzene                                                           3,3',4,4'-Benzophenonetetracarboxylic                                                            0.82 227                                4.75 kg (9.5 moles)  dianhydride                                               Bis(4-aminophenyl) ether                                                                            3.16 kg (9.85 moles)                                      0.101 kg (0.5 mole)                                                       8    1,4-Bis[4-(3-aminophenoxy)benzoyl]benzene                                                           3,3',4,4'-Biphenyltetracarboxylic                                                                0.84 230                                5.0 kg (10 moles)    dianhydride                                                                    2.90 kg (9.85 moles)                                 9    1,4-Bis[4-(3-aminophenoxy)benzoyl]benzene                                                           Pyromellitic dianhydride                                                                         0.80 248                                2.5 kg (5 moles)     2.14 kg (9.8 moles)                                       4,4'-Bis(3-aminophenoxy)biphenyl                                               1.84 kg (5 moles)                                                         10   1,4-Bis[4-(3-aminophenoxy)benzoyl]benzene                                                           Bis(3,4-dicarboxyphenyl) ether                                                                   0.78 220                                4.25 kg (8.5 moles)  dianhydride                                               Bis(4-aminophenyl) ether                                                                            3.038 kg (9.8 moles)                                      0.303 kg (1.5 moles)                                                      __________________________________________________________________________

EXAMPLES 42-45

The polyimide powder obtained in Synthesis Example 1 was dry blended with polyphenylene sulfide powder RYTON P-4 (Trade Mark; a product of Phillips Petroleum Co.) in various compositions as illustrated in Table 15. The mixture was kneaded by fusing at 320°-340° C. in an extruder having 40 mm aperture and a screw of 3.0/1 compression ratio, and extruded to obtain uniform pellets. The pellets thus obtained was injection molded at an injection temperature of 350°-390° C. and a mold temperature of 150° C. The physical and thermal properties of the molded product were measured and the results are illustrated in Table 15. In Table 15, tensile strength and elongation at break, flexural strength and flexural modulus, izod impact strength, and heat distortion temperature were respectively measured in accordance with ASTM D-638, D-790, D-256 and D-648.

Besides Table 15 also illustrates minimum injection pressure which indicates melt flowability. Lower minimum injection pressure results from better melt flowability.

COMPARATIVE EXAMPLE 15

The same procedures as Examples 42-45 were carried out by using a composition outside the scope of this invention. The physical and thermal properties of molded specimens were measured and the results are illustrated in Table 15.

                                      TABLE 15                                     __________________________________________________________________________     Example        Poly-                             Izod   Heat                   or             phenylene                                                                             Minimum                    impact distortion             Compara-                                                                             Polyimide                                                                               sulfide                                                                               injection                                                                           Tensile                                                                              Elonga-                                                                             Flexural                                                                             Flexural                                                                            strength                                                                              temperature            tive  Synthesis                                                                           (wt.                                                                               RYTON P-4                                                                             pressure                                                                            strength                                                                             tion strength                                                                             modulus                                                                             (notched)                                                                             (°C.)           example                                                                              example                                                                             parts)                                                                             (wt. parts)                                                                           (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        (%)  (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                            (18.6                  __________________________________________________________________________                                                             kg/cm.sup.2)           Ex. 42                                                                               1    98   2     480  1,650 60   2,800 36,300                                                                              21.0   215                    Ex. 43                                                                               1    85  15     260  1,640 55   2,800 38,000                                                                              20.6   214                    Ex. 44                                                                               1    75  25     190  1,600 45   2,740 40,000                                                                              19.9   212                    Ex. 45                                                                               1    50  50     *    1,520 33   2,560 41,200                                                                              18.4   200                    Comp. 15                                                                             1    100  0     550  1,650 60   2,800 36,300                                                                              21.0   215                    __________________________________________________________________________      *Lower than detection limit of 40 kg/cm.sup.2.                           

EXAMPLES 46-55 AND COMPARATIVE EXAMPLES 16-19

The procedures of Examples 42-45 were repeated by using the polyimide powder obtained in Synthesis Examples 2-5 to give uniformly blended pellets. The pellets were injection molded. Physical and thermal properties were measured on the molded specimens. The results on both within and outside the scope of this invention are illustrated in Tables 16-17 as Examples 46-55 and Comparative Examples 16-19, respectively.

                                      TABLE 16                                     __________________________________________________________________________     Example        Poly-                             Izod   Heat                   or             phenylene                                                                             Minimum                    impact distortion             Compara-                                                                             Polyimide                                                                               sulfide                                                                               injection                                                                           Tensile                                                                              Elonga-                                                                             Flexural                                                                             Flexural                                                                            strength                                                                              temperature            tive  Synthesis                                                                           (wt.                                                                               RYTON P-4                                                                             pressure                                                                            strength                                                                             tion strength                                                                             modulus                                                                             (notched)                                                                             (°C.)           example                                                                              example                                                                             parts)                                                                             (wt. parts)                                                                           (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        (%)  (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                            (18.6                  __________________________________________________________________________                                                             kg/cm.sup.2)           Ex. 46                                                                               2    95   5     420  1,350 39   1,800 36,500                                                                              15.7   210                    Ex. 47                                                                               2    75  25     160  1,340 38   1,800 39,800                                                                              15.6   209                    Ex. 48                                                                               2    50  50     *    1,270 35   1,740 41,100                                                                              15.0   208                    Comp. 16                                                                             2    100  0     580  1,350 40   1,800 36,000                                                                              16.0   210                    Ex. 49                                                                               3    95   5     560  1,150 100  1,530 34,000                                                                              18.0   233                    Ex. 50                                                                               3    75  25     230  1,100 85   1,500 38,600                                                                              17.8   228                    Ex. 51                                                                               3    50  50     *      990 60   1,500 41,200                                                                              16.2   216                    Comp. 17                                                                             3    100   0    650  1,150 100  1,530 32,400                                                                              18.3   235                    __________________________________________________________________________      *Lower than detection limit of 40 kg/cm.sup.2.                           

                                      TABLE 17                                     __________________________________________________________________________     Example        Poly-                             Izod   Heat                   or             phenylene                                                                             Minimum                    impact distortion             Compara-                                                                             Polyimide                                                                               sulfide                                                                               injection                                                                           Tensile                                                                              Elonga-                                                                             Flexural                                                                             Flexural                                                                            strength                                                                              temperature            tive  Synthesis                                                                           (wt.                                                                               RYTON P-4                                                                             pressure                                                                            strength                                                                             tion strength                                                                             modulus                                                                             (notched)                                                                             (°C.)           example                                                                              example                                                                             parts)                                                                             (wt. parts)                                                                           (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        (%)  (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                            (18.6                  __________________________________________________________________________                                                             kg/cm.sup.2)           Ex. 52                                                                               4    95   5     570  2,100 78   3,000 36,500                                                                              16.8   257                    Ex. 53                                                                               4    75  25     230  2,000 65   2,950 40,000                                                                              16     252                    Comp. 18                                                                             4    100  0     650  2,100 80   3,000 35,000                                                                              17.0   260                    Ex. 54                                                                               5    95   5     750  1,650 85   1,800 34,500                                                                              13.8   272                    Ex. 55                                                                               5    50  50     140  1,530 60   1,750 41,300                                                                              11.5   256                    Comp. 19                                                                             5    100  0     850  1,700 90   1,800 33,000                                                                              14.0   275                    __________________________________________________________________________

EXAMPLES 56-58

The polyimide powder obtained in Synthesis Example 6 was dry blended with polyphenylene sulfide RYTON P-4 in various compositions as illustrated in Table 18. The mixture was pelletized by extruding at 270°-310° C. with a twin screw extruder.

The pellets obtained were injection molded at the injection temperature of 280°-320° C. and mold temperature of 150° C. Physical and thermal properties of molded specimens were measured. Results are illustrated in Table 18.

COMPARATIVE EXAMPLE 20

The same procedures as Examples 42-44 were carried out by using a composition outside the scope of this invention. The physical and thermal properties of molded specimens were measured and the results are illustrated in Table 18.

                                      TABLE 18                                     __________________________________________________________________________     Example        Poly-                             Izod   Heat                   or             phenylene                                                                             Minimum                    impact distortion             Compara-                                                                             Polyimide                                                                               sulfide                                                                               injection                                                                           Tensile                                                                              Elonga-                                                                             Flexural                                                                             Flexural                                                                            strength                                                                              temperature            tive  Synthesis                                                                           (wt.                                                                               RYTON P-4                                                                             pressure                                                                            strength                                                                             tion strength                                                                             modulus                                                                             (notched)                                                                             (°C.)           example                                                                              example                                                                             parts)                                                                             (wt. parts)                                                                           (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        (%)  (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                            (18.6                  __________________________________________________________________________                                                             kg/cm.sup.2)           Ex. 56                                                                               6    95   5     320  1,590 70   1,960 38,000                                                                              16.4   220                    Ex. 57                                                                               6    75  25     200  1,560 65   1,900 40,200                                                                              15.5   217                    Ex. 58                                                                               6    50  50     *    1,450 50   1,820 41,800                                                                              13.5   209                    Comp. 20                                                                             6    100  0     520  1,600 70   1,960 37,500                                                                              16.5   220                    __________________________________________________________________________      *Lower than detection limit of 40 kg/cm.sup.2.                           

EXAMPLES 59-67 AND COMPARATIVE EXAMPLES 21-24

The procedures of Examples 56-58 were repeated by using the polyimide powder obtained in Synthesis Examples 7-10 to give uniformly blended pellets. The pellets were injection molded. Physical and thermal properties were measured on the molded specimens. The results on both within and outside the scope of this invention are illustrated in Tables 19-20 as Examples 59-67 and Comparative examples 21-24 respectively.

                                      TABLE 19                                     __________________________________________________________________________     Example        Poly-                             Izod   Heat                   or             phenylene                                                                             Minimum                    impact distortion             Compara-                                                                             Polyimide                                                                               sulfide                                                                               injection                                                                           Tensile                                                                              Elonga-                                                                             Flexural                                                                             Flexural                                                                            strength                                                                              temperature            tive  Synthesis                                                                           (wt.                                                                               RYTON P-4                                                                             pressure                                                                            strength                                                                             tion strength                                                                             modulus                                                                             (notched)                                                                             (°C.)           example                                                                              example                                                                             parts)                                                                             (wt. parts)                                                                           (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        (%)  (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                            (18.6                  __________________________________________________________________________                                                             kg/cm.sup.2)           Ex. 59                                                                               7    95   5     340  1,850 68   1,980 38,000                                                                              15.5   204                    Ex. 60                                                                               7    50  50     *    1,770 62   1,930 41,800                                                                              13.0   195                    Comp. 21                                                                             7    100  0     560  1,850 68   1,980 38,000                                                                              15.5   204                    Ex. 61                                                                               8    95   5     300  1,390 60   1,700 35,800                                                                              12.3   210                    Ex. 62                                                                               8    50  50     *    1,300 50   1,650 41,400                                                                              10.5   198                    Comp. 22                                                                             8    100  0     510  1,400 60   1,700 34,500                                                                              12.5   210                    Ex. 63                                                                               9    90  10     360  1,490 83   1,750 36,100                                                                              17.0   231                    Ex. 64                                                                               9    50  50     *    1,400 60   1,690 41,000                                                                              13.5   222                    Comp. 23                                                                             9    100 0      620  1,500 85   1,750 35,200                                                                              17.5   231                    __________________________________________________________________________      *Lower than detection limit of 40 kg/cm.sup.2.                           

                                      TABLE 20                                     __________________________________________________________________________     Example        Poly-                             Izod   Heat                   or             phenylene                                                                             Minimum                    impact distortion             Compara-                                                                             Polyimide                                                                               sulfide                                                                               injection                                                                           Tensile                                                                              Elonga-                                                                             Flexural                                                                             Flexural                                                                            strength                                                                              temperature            tive  Synthesis                                                                           (wt.                                                                               RYTON P-4                                                                             pressure                                                                            strength                                                                             tion strength                                                                             modulus                                                                             (notched)                                                                             (°C.)           example                                                                              example                                                                             parts)                                                                             (wt. parts)                                                                           (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        (%)  (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                            (18.6                  __________________________________________________________________________                                                             kg/cm.sup.2)           Ex. 65                                                                               10   95   5     360  1,350 64   1,460 31,400                                                                              11.5   201                    Ex. 66                                                                               10   85  15     240  1,340 62   1,460 34,000                                                                              11.0   199                    Ex. 67                                                                               10   75  25     150  1,330 59   1,440 36,000                                                                              10.0   195                    Comp. 24                                                                             10   100  0     580  1,350 65   1,460 30,000                                                                              11.5   201                    __________________________________________________________________________

EXAMPLES 68-71

The polyimide powder obtained in Synthesis Example 1 was dry blended with aromatic polysulfone powder VICTREX PES 3600P (Trade Mark; a product of Imperial Chemical Industry) in various compositions as illustrated in Table 21. The mixture was kneaded by fusing at 330°-360° C. in an extruder having 40 mm aperture and a screw of 3.0/1 compression ratio, and extruded to obtain uniform pellets. The pellets thus obtained were injection molded at an injection temperature of 360° C. and a mold temperature of 180° C. The physical and thermal properties of the molded product were measured and the results are illustrated in Table 21.

In Table 21, the glass transition temperature Tg which was measured in accordance with TMA penetration method is also illustrated.

COMPARATIVE EXAMPLE 25

The same procedures as Examples 68-71 were carried out by using a composition outside the scope of this invention. The physical and thermal properties of molded specimens were measured and the results are illustrated in Table 21.

                                      TABLE 21                                     __________________________________________________________________________     Example         Aromatic                       Izod  Heat                      or              Polysulfone                                                                          Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide VICTREX                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. PES 3600P                                                                            pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 68                                                                               1    95    5    500  1,650                                                                               60   2,800                                                                               36,300                                                                              21.0  215    235                Ex. 69                                                                               1    85   15    450  1,650                                                                               60   2,800                                                                               36,300                                                                              21.0  215    235                Ex. 70                                                                               1    75   25    380  1,600                                                                               60   2,750                                                                               36,000                                                                              20.2  213    234                Ex. 71                                                                               1    50   50    320  1,480                                                                               60   2,550                                                                               34,500                                                                              19.0  211    231                Comp. 25                                                                             1    100   0    550  1,650                                                                               60   2,800                                                                               36,300                                                                              21.0  215    235                __________________________________________________________________________

EXAMPLES 72-74 AND COMPARATIVE EXAMPLE 26

The polyimide powder obtained in Synthesis Example 2 was dry blended with aromatic polysulfone VICTREX PES 3600P in the compositions illustrated in Table 22 and pelletized by the same procedures as Examples 67-70 at 320°-360° C. The pellets obtained were injection molded at 380° C. with a mold temperature of 190° C. Physical and thermal properties of molded specimens were measured. Results are illustrated in Table 22.

                                      TABLE 22                                     __________________________________________________________________________     Example         Aromatic                       Izod  Heat                      or              Polysulfone                                                                          Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide VICTREX                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. PES 3600P                                                                            pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 72                                                                               2    95    5    465  1,350                                                                               40   1,800                                                                               36,000                                                                              16.0  210    235                Ex. 73                                                                               2    75   25    395  1,300                                                                               45   1,800                                                                               35,000                                                                              15.0  207    233                Ex. 74                                                                               2    50   50    335  1,200                                                                               50   1,750                                                                               33,500                                                                              13.5  205    230                Comp. 26                                                                             2    100   0    580  1,350                                                                               40   1,800                                                                               36,000                                                                              16.0  210    235                __________________________________________________________________________

EXAMPLES 75-77 AND COMPARATIVE EXAMPLE 27

The polyimide powder obtained in Synthesis Example 3 was dry blended with aromatic polysulfone powder UDEL POLYSULFONE P-1700 (Trade Mark; a product of Union Carbide Corp.) in various compositions as illustrated in Table 23. The mixture was kneaded by fusing at 360°-390° C. in an extruder having 40 mm aperture and a screw of 3.0/1 compression ratio, and extruded to obtain uniform pellets. The pellets thus obtained was injection molded at an injection temperature of 390° C. and a mold temperature of 190° C. The physical and thermal properties of the molded product were measured and the results are illustrated in Table 23.

                                      TABLE 23                                     __________________________________________________________________________                     Aromatic                                                                       Polysulfone                                                    Example         UDEL                           Izod  Heat                      or              POLY- Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide SULFONE                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. P-1700                                                                               pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 75                                                                               3    95    5    520  1,120                                                                               100  1,520                                                                               32,400                                                                              18.3  235    253                Ex. 76                                                                               3    85   15    440  1,100                                                                               100  1,520                                                                               32,400                                                                              17.9  233    250                Ex. 77                                                                               3    50   50    350  1,000                                                                               100  1,460                                                                               32,000                                                                              16.5  202    223                Comp. 27                                                                             3    100   0    650  1,150                                                                               100  1,530                                                                               32,400                                                                              18.3  235    255                __________________________________________________________________________

EXAMPLES 78-80 AND COMPARATIVE EXAMPLE 28

The same procedures as Examples 68-71 were carried out to obtain uniformly blended pellets except that the polyimide powder obtained in Synthesis Example 4 and UDEL POLYSULFONE P-1700 were treated at 370°-390° C.

The pellets obtained were injection molded at 390° C. with a mold temperature of 180° C. Physical and thermal properties of molded specimens were measured. Results are illustrated in Table 24.

                                      TABLE 24                                     __________________________________________________________________________                     Aromatic                                                                       Polysulfone                                                    Example         UDEL                           Izod  Heat                      or              POLY- Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide SULFONE                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. P-1700                                                                               pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 78                                                                               4    95    5    600  2,080                                                                               80   3,000                                                                               35,000                                                                              17.0  260    285                Ex. 79                                                                               4    75   25    480  2,000                                                                               80   3,000                                                                               35,000                                                                              16.5  255    280                Ex. 80                                                                               4    50   50    330  1,850                                                                               80   2,800                                                                               34,200                                                                              15.5  252    275                Comp. 28                                                                             4    100   0    650  2,100                                                                               80   3,000                                                                               35,000                                                                              17.0  260    285                __________________________________________________________________________

EXAMPLES 81-83 AND COMPARATIVE EXAMPLE 29

The same procedures as Examples 68-71 were carried out to obtain uniformly blended pellets except that the polyimide powder obtained in Synthesis Example 5 and aromatic polysulfone VICTREX PES 3600P were treated at 370°-390° C.

The pellets obtained were injection molded at 390° C. with a mold temperature of 180° C. Physical and thermal properties of molded specimens were measured. Results are illustrated in Table 25.

                                      TABLE 25                                     __________________________________________________________________________     Example         Aromatic                       Izod  Heat                      or              Polysulfone                                                                          Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide VICTREX                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. PES 3600P                                                                            pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 81                                                                               5    95    5    800  1,700                                                                               90   1,800                                                                               33,000                                                                              14.0  274    293                Ex. 82                                                                               5    75   25    600  1,660                                                                               90   1,780                                                                               33,000                                                                              12.0  270    289                Ex. 83                                                                               5    50   50    450  1,580                                                                               90   1,700                                                                               31,000                                                                              10.0  261    282                Comp. 29                                                                             5    100   0    850  1,700                                                                               90   1,800                                                                               33,000                                                                              14.0  275    295                __________________________________________________________________________

EXAMPLES 84-86

The polyimide powder obtained in Synthesis Example 6 was dry blended with aromatic polysulfone powder UDEL POLYSULFONE P-1700 in various compositions as illustrated in Table 26. The mixture was pelletized by extruding at 300°-330° C. with a twin screw extruder.

The pellets obtained were injection molded at the cylinder temperature of 330°-360° C. and mold temperature of 150° C. Physical and thermal properties of molded specimens were measured. Results are illustrated in Table 26.

COMPARATIVE EXAMPLE 30

The sample procedures as Examples 84-86 were carried out by using a composition outside the scope of this invention. The physical and thermal properties of molded specimens were measured and the results are illustrated in Table 26.

                                      TABLE 26                                     __________________________________________________________________________                     Aromatic                                                                       Polysulfone                                                    Example         UDEL                           Izod  Heat                      or              POLY- Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide SULFONE                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. P-1700                                                                               pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 84                                                                               6    95    5    420  1,600                                                                               72   1,960                                                                               37,500                                                                              16.5  219    238                Ex. 85                                                                               6    75   25    310  1,580                                                                               90   1,950                                                                               37,200                                                                              16.0  216    236                Ex. 86                                                                               6    50   50    275  1,500                                                                               98   1,880                                                                               36,100                                                                              14.8  210    230                Comp. 30                                                                             6    100   0    520  1,600                                                                               70   1,960                                                                               37,500                                                                              16.5  220    238                __________________________________________________________________________

EXAMPLES 87-94 AND COMPARATIVE EXAMPLES 31-34

The polyimide powder obtained in Synthesis Examples 7-10 was mixed with aromatic polysulfone. VICTREX PES 3600P and UDEL POLYSULFONE P-1700 are used as aromatic polysulfone. The resulting mixtures having compositions illustrated in Tables 27-29 were kneaded by fusing in an extruder to obtain uniformly blended pellets.

The pellets above obtained were injection molded with the same conditions as Examples 84-86. The molded specimens were measured their physical and thermal properties. The results obtained are illustrated in Tables 27-29.

                                      TABLE 27                                     __________________________________________________________________________                     Aromatic                                                                       Polysulfone                                                    Example         UDEL                           Izod  Heat                      or              POLY- Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide SULFONE                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. P-1700                                                                               pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 87                                                                               7    95   5     470  1,850                                                                               72   1,980                                                                               38,000                                                                              15.0  204    228                Ex. 88                                                                               7    50   50    290  1,730                                                                               95   1,850                                                                               36,800                                                                              14.2  202    226                Comp. 31                                                                             7    100  0     560  1,850                                                                               68   1,980                                                                               38,000                                                                              15.5  204    228                __________________________________________________________________________

                                      TABLE 28                                     __________________________________________________________________________     Example         Aromatic                       Izod  Heat                      or              Polysulfone                                                                          Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide VICTREX                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. PES 3600P                                                                            pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 89                                                                               8    90   10    410  1,390                                                                               61   1,700                                                                               34,300                                                                              12.5  210    230                Ex. 90                                                                               8    50   50    300  1,370                                                                               64   1,650                                                                               33,500                                                                              11.5  207    228                Comp. 32                                                                             8    100   0    510  1,400                                                                               60   1,700                                                                               34,500                                                                              12.5  210    230                Ex. 91                                                                               9    95    5    480  1,500                                                                               85   1,740                                                                               35,200                                                                              17.0  231    250                Ex. 92                                                                               9    50   50    310  1,420                                                                               80   1,710                                                                               34,100                                                                              16.0  227    247                Comp. 33                                                                             9    100   0    620  1,500                                                                               85   1,750                                                                               35,200                                                                              17.5  231    250                __________________________________________________________________________

                                      TABLE 29                                     __________________________________________________________________________                     Aromatic                                                                       Polysulfone                                                    Example         UDEL                           Izod  Heat                      or              POLY- Minimum                  impact                                                                               distortion                Compara-                                                                             Polyimide SULFONE                                                                              injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                            Flexural                                                                            strength                                                                             temperature               tive  Synthesis                                                                           (wt. P-1700                                                                               pressure                                                                            strength                                                                            tion strength                                                                            modulus                                                                             (notched)                                                                            (°C.)                                                                          Tg                 example                                                                              example                                                                             parts)                                                                              (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                           (18.6                                                                                 (°C.)       __________________________________________________________________________     Ex. 93                                                                               10   95   5     435  1,350                                                                               68   1,460                                                                               30,000                                                                              11.5  201    220                Ex. 94                                                                               10   50   50    260  1,250                                                                               90   1,410                                                                               28,000                                                                              10.0  197    214                Comp. 34                                                                             10   100  0     580  1,350                                                                               65   1,460                                                                               30,000                                                                              11.5  201    220                __________________________________________________________________________

EXAMPLES 95-106

The polyimide powder obtained in Synthesis Examples 6-10 was dry blended with the commercially available aromatic polyetherimide ULTEM 1000 (Trade Mark; a product of General Electric Co. in U.S.A.) in various compositions as illustrated in Tables 30-32. The mixture was pelletized by extruding at 370°-400° C. with a twin screw extruder.

The pellets obtained were injection molded at the cylinder temperature of 360°-390° C. and mold temperature of 150° C. Physical and thermal properties of molded specimens were measured. Results are illustrated in Tables 30-32.

COMPARATIVE EXAMPLES 35-39

The same procedures as Examples 95-106 were carried out by using a composition outside the scope of this invention. The physical and thermal properties of molded specimens were measured and the results are illustrated in Tables 30-32.

                                      TABLE 30                                     __________________________________________________________________________                      Aromatic                                                      Example          polyether-                      Izod   Heat                   or               imide Minimum                   impact distortion             Compara-                                                                             Polyimide  ULTEM-                                                                               injection                                                                           Tensile                                                                             Elonga-                                                                             Flexural                                                                             Flexural                                                                            strength                                                                              temperature            tive  Synthesis  1000  pressure                                                                            strength                                                                            tion strength                                                                             modulus                                                                             (notched)                                                                             (°C.)           example                                                                              example                                                                             (wt. parts)                                                                          (wt. parts)                                                                          (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (kg cm/cm)                                                                            (18.6                  __________________________________________________________________________                                                             kg/cm.sup.2)           Ex. 95                                                                               6    95     5    510  1,580                                                                               70   1,950 37,300                                                                              16.2   219                    Ex. 96                                                                               6    85    15    480  1,560                                                                               68   1,930 37,100                                                                              15.7   218                    Ex. 97                                                                               6    75    25    455  1,530                                                                               67   1,900 36,800                                                                              15.0   217                    Ex. 98                                                                               6    50    50    410  1,430                                                                               65   1,800 36,100                                                                              12.7   212                    Comp. 35                                                                             6    100    0    520  1,600                                                                               70   1,960 37,500                                                                              16.5   220                    __________________________________________________________________________

                                      TABLE 31                                     __________________________________________________________________________     Example       Aromatic                           Izod  Heat                    or     Polymide                                                                              polyether-                                                                            Minimum                     impact                                                                               distortion              Compara-                                                                              Synthesis                                                                             imide  injection                                                                            Tensile                                                                             Elonga-                                                                              Flexural                                                                            Flexural                                                                             strength                                                                             temperature             tive   example                                                                               ULTEM-1000                                                                            pressure                                                                             strength                                                                            tion  strength                                                                            modulus                                                                              (notched)                                                                            (°C.)            example                                                                               (wt. parts)                                                                           (wt. parts)                                                                           (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (%)   (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        (kg cm/cm)                                                                           (18.6                   __________________________________________________________________________                                                            kg/cm.sup.2)            Ex. 99 7  90  10     510   1,810                                                                               67    1,960                                                                               37,700                                                                               15.0  203                     Ex. 100                                                                               7  50  50     415   1,600                                                                               63    1,820                                                                               36,500                                                                               12.0  201                     Comp. 36                                                                              7  100  0     560   1,850                                                                               68    1,980                                                                               38,000                                                                               15.5  204                     Ex. 101                                                                               8  70  30     435   1,350                                                                               60    1,670                                                                               34,300                                                                               11.0  208                     Ex. 102                                                                               8  50  50     405   1,300                                                                               60    1,630                                                                               34,000                                                                                9.5  206                     Comp. 37                                                                              8  100  0     510   1,400                                                                               60    1,700                                                                               34,500                                                                               12.5  210                     __________________________________________________________________________

                                      TABLE 32                                     __________________________________________________________________________     Example       Aromatic                           Izod  Heat                    or     Polymide                                                                              polyether-                                                                            Minimum                     impact                                                                               distortion              Compara-                                                                              Synthesis                                                                             imide  injection                                                                            Tensile                                                                             Elonga-                                                                              Flexural                                                                            Flexural                                                                             strength                                                                             temperature             tive   example                                                                               ULTEM-1000                                                                            pressure                                                                             strength                                                                            tion  strength                                                                            modulus                                                                              (notched)                                                                            (°C.)            example                                                                               (wt. parts)                                                                           (wt. parts)                                                                           (kg/cm.sup.2)                                                                        (kg/cm.sup.2)                                                                       (%)   (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        (kg cm/cm)                                                                           (18.6                   __________________________________________________________________________                                                            kg/cm.sup.2)            Ex. 103                                                                                9 95   5     570   1,490                                                                               84    1,750                                                                               35,200                                                                               17.2  231                     Ex. 104                                                                                9 75  25     505   1,450                                                                               82    1,710                                                                               35,000                                                                               16.0  226                     Comp. 38                                                                               9 100  0     620   1,500                                                                               85    1,750                                                                               35,200                                                                               17.5  231                     Ex. 105                                                                               10 75  25     465   1,310                                                                               64    1,470                                                                               30,600                                                                               10.3  200                     Ex. 106                                                                               10 50  50     415   1,270                                                                               62    1,470                                                                               31,400                                                                                9.0  200                     Comp. 39                                                                              10 100  0     580   1,350                                                                               65    1,460                                                                               30,000                                                                               11.5  201                     __________________________________________________________________________

SYNTHESIS EXAMPLE 1 OF THE POLYIMIDE OF THE FOURTH ASPECT OF THE INVENTION

In a reaction flask filled with a stirrer, a reflux condenser and a nitrogen introducing tube were placed 3.66 kg (10 moles) of 4,4'-bis(3-aminophenoxy)biphenyl and 52.15 kg of N,N-dimethylacetamide, followed by addition of 2.11 kg (9.7 mols) of pyromellitic dianhydride at room temperature in nitrogen atmosphere with attention paid to elevation of the temperature of the solution. Then stirring was continued at room temperature for about 20 hours.

To this polyamide acid solution, 2.20 kg (20 mols) of triethylamine and 3.06 kg (30 mols) of acetic anhydride were dropped at room temperature in nitrogen atmosphere. After 20 hours of stirring, there was produced a yellow slurry, which was filtered off to yield a light yellow polyimide powder. To the resultant powder, methanol was added to produce a sludge, which was filtered off and dried at 180° C. under reduced pressure for 8 hours to yield 5.36 kg of polyimide powder.

The thus-obtained polyimide powder had a inherent viscosity of 0.50 dl/g, as determined in the procedure: polyimide powder (0.5 g) was dissolved in 100 ml of solvent with heating, then allowed to cool to 35° C. and measured with a mixture of p-chlorophenol and phenol (90:10 parts/parts by weight) as solvent.

The glass transition temperature of the powder was 256° C. as measured according to DSC and the thermal decomposition temperature 5% at 560° C. as measured according to DTA-TG.

SYNTHESIS EXAMPLES 2 TO 4

With different diamines and different tetracarboxylic dianhydrides in varying combination powders of various polyimides were obtained in the same process as described in Synthesis Example 1.

Table 33 gives a summary of Synthesis Examples 1 through 4 which includes synthesis conditions of polyimide resins, and inherent viscosities of the produced polyimide powders. It includes the conditions for preparation in Synthesis Example 1 and the physical properties of the produced polyimide powder.

                  TABLE 33                                                         ______________________________________                                                            Tetracarboxylic                                                                             Inherent                                       Diamine            dianhydride  viscosity                                      Name, kg (mol)     Name, kg (mol)                                                                              (dl/g)                                         ______________________________________                                         Synthesis                                                                             4,4'-bis(3-amino-                                                                              Pyromellitic 0.50                                       1      phenoxy)biphenyl                                                                               dianhydride                                                    3,68 kg (10 mol)                                                                               2.11 kg (9.7 mol)                                       Synthesis                                                                             4,4'-bis(3-amino-                                                                              4,4'-(p-phenylene-                                                                          0.52                                       2      phenoxy)biphenyl                                                                               dioxy)diphthalic                                               3.68 kg (10 mol)                                                                               dianhydride                                                                    3.92 kg (9.75 mol)                                      Synthesis                                                                             Bis[4-(3-amino- Pyromellitic 0.49                                       3      phenoxy)phenyl]sulfide                                                                         dianhydride                                                    4.0 kg (10 mol) 2.11 kg (9.7 mol)                                       Synthesis                                                                             Bis[4-(3-amino- 3,3',4,4'-biphenyl-                                                                         0.50                                       4      phenoxy)phenyl]sulfide                                                                         tetracarboxylic                                                4.0 kg (10 mol) dianhydride                                                                    2.87 kg (9.7 mol)                                       ______________________________________                                    

SYNTHESIS EXAMPLE 5

In a reaction flask, which is similar to that used in Synthesis Example 1, were placed 5 kg (10 mols) of 1,3-bis[4-(3-aminophenoxy)benzoyl]benzene and 40.1 kg of N,N-dimethylacetoamide, and cooled to about 0° C., to which 5 portions (a total of 2,082 kg (9.55 mols)) of pyromellitic dianhydride were added in sequence in nitrogen atmosphere with attention paid to elevation of the temperature of the solution. Stirring was continued for about 2 hours. Subsequently the solution was cooled to room temperature, followed by about 20 hours' further stirring in nitrogen atmosphere.

To this polyamide acid solution 2,20 kg (20 mols) of triethylamine and 2.55 kg (25 mols) acetic anhydride were dripped at room temperature in nitrogen atmosphere. After 20 hours' stirring, there was produced a yellow slurry, which was filtered off to yield a light yellow polyimide powder. To the resultant powder, methanol was added to produce a sludge, which was filtered off and dried at 150° C. under reduced pressure for 8 hours to obtain 6.5 kg (yield: about 97.5%) of light yellow polyimide powder. The glass transition temperature of this powder was 235° C. as measured according DSC, and the inherent viscosity was 0.53 dl/g.

SYNTHESIS EXAMPLES 6 TO 9

With different diamines and different tetracarboxylic acid dianhydrides in varying combinations, powders of various polyimides were obtained in the same process as described in Synthesis Example 5. Table 34 gives a summary of Synthesis Examples 5 through 9 which includes synthesis conditions and inherent viscosities of the obtained polyimide powders.

                  TABLE 34                                                         ______________________________________                                                            Tetracarboxylic                                                                             Inherent                                       Diamine            dianhydride  viscosity                                      Name, kg (mol)     Name, kg (mol)                                                                              (dl/g)                                         ______________________________________                                         Synthesis                                                                             1,3-bis[4-(3-   Pyromellitic 0.53                                       5      phenoxy)benzoyl]                                                                               dianhydride                                                    benzene         2.082 kg                                                       5 kg (10 mol)   (9.55 mol)                                              Synthesis                                                                             1,3-bis[4-(3-amino-                                                                            3,3',4,4'-   0.51                                       6      phenoxy)benzoyl]                                                                               benzophenon-                                                   benzene         tetracarboxylic                                                4.75 kg (9.5 mol)                                                                              3,05 kg (9.52 mol)                                             Bis(4-aminophenyl)ether                                                        0.101 kg (0.5 mol)                                                      Synthesis                                                                             1,4-bis[4-(3-amino-                                                                            3,3',4,4'-biphenyl-                                                                         0.52                                       7      phenoxy)benzoyl]                                                                               tetracarboxylic                                                benzene         dianhydride                                                    5.0 kg (10 mol) 2.81 kg (9.55 mol)                                      Synthesis                                                                             1,4-bis[4-(3-amino-                                                                            Pyromellitic 0.49                                       8      phenoxy)benzoyl]                                                                               dianhydride                                                    benzene         2.07 kg (9.5 mol)                                              2.5 kg (5 mol)                                                                 4,4'-bis(3-amino-                                                              phenoxy) biphenyl                                                              1.84 kg (5 mol)                                                         Synthesis                                                                             1,4-bis[4-(3-amino-                                                                            Bis(3,4-dicarboxy-                                                                          0.45                                       9      phenoxy)benzoyl]                                                                               phenyl)ether                                                   benzene         dianhydride                                                    4.25 kg (8.5 mol)                                                                              2.93 kg (9.45 mol)                                             Bis(4-aminophenyl)ether                                                        0.303 kg (1.5 mol)                                                      ______________________________________                                    

EXAMPLES 107 THROUGH 131

Dry-blends of a polyimide powder obtained in any of Synthesis Examples 1 through 9 with an aromatic polyamideimide powder TORLON 4203L^(R) (Amoco Chemicals Corp., USA) commercially available in varying compositions summarized in Tables 34 through 36 were extruded, simultaneously with melting, mixing and kneading, to form uniformly-mixed pellets.

Subsequently in thus-obtained uniformly-mixed pellet was molded in an injection molding machine (Arburg All-Round A-20) under conditions of melt-mold temperature 220° C. and barrel temperature 380 to 400° C. The molded test pieces were measured for their physical and thermal properties.

The obtained results are given in Tables 35 through 40.

The individual Tables include minimum injection molding pressures as well.

Data in the Tables were obtained as follows: tensile strength and elongation at break according to ASTM D-638, flexural strength and flexural modulus according to ASTM D-790 Izod impact strength according to D-256, glass transition temperature according to the TMA needle-insertion method, and heat distortion temperature according to ASTM D-648.

COMPARATIVE EXAMPLES 40 THROUGH 49

With other compositions out of the scope of the fourth aspect of the invention and in the same way as in Examples 107 through 131, molded products were obtained and the measured results of their physical and thermal properties are given Tables 35 through 40.

                                      TABLE 35                                     __________________________________________________________________________                                                               Heat                                     Aroma-                                distor-                                  tic   Minimum                         tion                                     poly- injec-                     Notched                                                                             tem-                                     amide-                                                                               tion       Elong-          Izod pera-                                    imide pres-      ation           impact                                                                              ture                                     TORLON                                                                               sure  Tensile                                                                             at   Flexural                                                                            Flexural                                                                             strength                                                                            (°C.)                 Polyimide   4203L (kg/cm.sup.2)                                                                        strength                                                                            break                                                                               strength                                                                            modulus                                                                              (kg-cm/                                                                             (18.6                        Product                                                                              Amount                                                                               Amount                                                                               *     (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        cm)  kg/cm.sup.2)         __________________________________________________________________________     Example 107                                                                            Product of                                                                           95     5    460   1250 98   1620 34500 18.3 240                  Example 108                                                                            Synthesis                                                                            85    15    465   1440 95   1770 37400 17.9 250                  Example 109                                                                            1     75    25    480   1530 93   1860 40000 17.6 258                  Example 110   50    50    500   1730 81   2050 44000 17.0 268                  Compara-      100    0    460   1100 100  1530 32400 18.3 235                  tive                                                                           example 40                                                                     Example 111                                                                            Product of                                                                           90    10    380   1390 10   1610 35400 12.5 198                  Example 112                                                                            Synthesis                                                                            50    50    440   1710 10   2000 43600 13.0 254                  Compara-                                                                               2     100    0    380   1230 10   1450 32100 12.5 181                  tive                                                                           example 41                                                                     __________________________________________________________________________      *: Lower melt viscosity, lower minimum injection pressure. The rest is th      same.                                                                    

                                      TABLE 36                                     __________________________________________________________________________                                                               Heat                                     Aroma-                                distor-                                  tic   Minimum                         tion                                     poly- injec-                     Notched                                                                             tem-                                     amide-                                                                               tion       Elong-          Izod pera-                                    imide pres-      ation           impact                                                                              ture                                     TORLON                                                                               sure  Tensile                                                                             at   Flexural                                                                            Flexural                                                                             strength                                                                            (°C.)                 Polyimide   4203L (kg/cm.sup.2)                                                                        strength                                                                            break                                                                               strength                                                                            modulus                                                                              (kg-cm/                                                                             (18.6                        Product                                                                              Amount                                                                               Amount                                                                               *     (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        cm)  kg/cm.sup.2)         __________________________________________________________________________     Example 113                                                                            Product of                                                                           90    10    430   1600 57   1700  400  20.4 225                  Example 114                                                                            Synthesis                                                                            75    25    445   1670 53   1820 32400 19.8 236                  Example 115                                                                            3     50    50    485   1780 43   1970 38900 18.3 251                  Compara-      100    0    420   1550 60   1600 25500 21.0 215                  tive                                                                           example 42                                                                     __________________________________________________________________________

                                      TABLE 37                                     __________________________________________________________________________                                                               Heat                                     Aroma-                                distor-                                  tic   Minimum                         tion                                     poly- injec-                     Notched                                                                             tem-                                     amide-                                                                               tion       Elong-          Izod pera-                                    imide pres-      ation           impact                                                                              ture                                     TORLON                                                                               sure  Tensile                                                                             at   Flexural                                                                            Flexural                                                                             strength                                                                            (°C.)                 Polyimide   4203L (kg/cm.sup.2)                                                                        strength                                                                            break                                                                               strength                                                                            modulus                                                                              (kg-cm/                                                                             (18.6                        Product                                                                              Amount                                                                               Amount                                                                               *     (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        cm)  kg/cm.sup.2)         __________________________________________________________________________     Example 116                                                                            Product of                                                                           85    15    420   1320 34   1500 26800 11.5 202                  Example 117                                                                            Synthesis                                                                            50    50    450   1570 28   1800 37000 12.1 241                  Compara-                                                                               4     100    0    410   1150 35   1350 22000 11.0 185                  tive                                                                           example 43                                                                     __________________________________________________________________________

                                      TABLE 38                                     __________________________________________________________________________                                                               Heat                                     Aroma-                                distor-                                  tic   Minimum                         tion                                     poly- injec-                     Notched                                                                             tem-                                     amide-                                                                               tion       Elong-          Izod pera-                                    imide pres-      ation           impact                                                                              ture                                     TORLON                                                                               sure  Tensile                                                                             at   Flexural                                                                            Flexural                                                                             strength                                                                            (°C.)                 Polyimide   4203L (kg/cm.sup.2)                                                                        strength                                                                            break                                                                               strength                                                                            modulus                                                                              (kg-cm/                                                                             (18.6                        Product                                                                              Amount                                                                               Amount                                                                               *     (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        cm)  kg/cm.sup.2)         __________________________________________________________________________     Example 118                                                                            Product of                                                                           95     5    310   1650 68   1990 38800 16.5 230                  Example 119                                                                            Synthesis                                                                            85    15    320   1730 65   2030 41200 16.4 244                  Example 120                                                                            5     75    25    330   1790 61   2070 42800 16.4 254                  Example 121   50    50    360   1880 48   2120 45200 16.0 267                  Compara-      100    0    310   1600 70   1960 37500 16.5 220                  tive                                                                           example 44                                                                     Compara-       0    100   610   1920 13   2150 47000 14.0 275                  tive                                                                           example 45                                                                     __________________________________________________________________________      *: Lower melt viscosity, lower minimum injection pressure. The rest is th      same.                                                                    

                                      TABLE 39                                     __________________________________________________________________________                                                               Heat                                     Aroma-                                distor-                                  tic   Minimum                         tion                                     poly- injec-                     Notched                                                                             tem-                                     amide-                                                                               tion       Elong-          Izod pera-                                    imide pres-      ation           impact                                                                              ture                                     TORLON                                                                               sure  Tensile                                                                             at   Flexural                                                                            Flexural                                                                             strength                                                                            (°C.)                 Polyimide   4203L (kg/cm.sup.2)                                                                        strength                                                                            break                                                                               strength                                                                            modulus                                                                              (kg-cm/                                                                             (18.6                        Product                                                                              Amount                                                                               Amount                                                                               *     (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        cm)  kg/cm.sup.2)         __________________________________________________________________________     Example 122                                                                            Product of                                                                           90    10    365   1870 66   2020 40800 15.5 226                  Example 123                                                                            Synthesis                                                                            75    25    380   1900 60   2070 41800 15.5 248                  Example 124                                                                            6     50    50    405   1920 46   2130 45800 15.3 264                  Compara-      100    0    360   1850 68   1980 38000 15.5 204                  tive                                                                           example 46                                                                     Example 125                                                                            Product of                                                                           85    15    335   1610 59   1870 41700 13.0 237                  Example 126                                                                            Synthesis                                                                            50    50    380   1830 48   2070 44700 13.8 263                  Compara-                                                                               7     100    0    320   1400 60   1700 34500 12.5 210                  tive                                                                           example 47                                                                     __________________________________________________________________________

                                      TABLE 40                                     __________________________________________________________________________                                                               Heat                                     Aroma-                                distor-                                  tic   Minimum                         tion                                     poly- injec-                     Notched                                                                             tem-                                     amide-                                                                               tion       Elong-          Izod pera-                                    imide pres-      ation           impact                                                                              ture                                     TORLON                                                                               sure  Tensile                                                                             at   Flexural                                                                            Flexural                                                                             strength                                                                            (°C.)                 Polyimide   4203L (kg/cm.sup.2)                                                                        strength                                                                            break                                                                               strength                                                                            modulus                                                                              (kg-cm/                                                                             (18.6                        Product                                                                              Amount                                                                               Amount                                                                               *     (kg/cm.sup.2)                                                                       (%)  (kg/cm.sup.2)                                                                       (kg/cm.sup.2)                                                                        cm)  kg/cm.sup.2)         __________________________________________________________________________     Example 127                                                                            Product of                                                                           90    10    425   1620 83   1870 39000 17.4 242                  Example 128                                                                            Synthesis                                                                            75    25    435   1730 80   1980 42400 17.2 254                  Example 129                                                                            8     50    50    460   1860 67   2090 45400 16.6 266                  Compara-      100    0    420   1500 85   1750 35200 17.5 231                  tive                                                                           example 48                                                                     Example 130                                                                            Product of                                                                           85    15    360   1560 64   1730 37000 12.5 230                  Example 131                                                                            Synthesis                                                                            50    50    400   1820 53   2020 43800 13.7 260                  Compara-                                                                               9     100    0    350   1350 65   1460 30000 11.5 201                  tive                                                                           example 49                                                                     __________________________________________________________________________

Other embodiments of the various aspects of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the aspects of the invention disclosed herein. It is intended that the specification and examples be considered as exemplary only, with the true scope and spirit of the aspects of the invention being indicated by the claims. 

What is claimed is:
 1. A resin composition which comprises 99.9 to 50% by weight of a polyimide and 0.1 to 50% by weight of an aromatic polyamideimide based on the total amount of said polyimide and said aromatic polyamideimide, said polyimide having a recurring unit which does not include amide moieties and which is represented by the formula: ##STR42## where Z indicates a direct bond or is ##STR43## ##STR44## and Y is a tetravalent group selected from the group consisting of an aliphatic group having at least 2 carbon atoms, an alicyclic group, a monocyclic aromatic group, a fused polycyclic aromatic group, and a polycyclic aromatic group where aromatic groups are linked to one another directly or via a bridge member.
 2. A resin composition defined in claim 1 wherein Y in said formula is a tetravalent group selected from the group consisting of groups represented by ##STR45##
 3. A resin composition defined in claim 1 wherein said aromatic polyamideimide is a polymer having a recurring unit represented by the formula: ##STR46## where Ar₃ is a trivalent aromatic radical having at least one benzene ring, and J is a divalent organic group.
 4. A resin composition defined in claim 1 wherein the content of said polyimide is 99.5 to 50% by weight and the content of said aromatic polyamideimide is 0.5 to 50% by weight.
 5. A resin composition defined in claim 1 wherein said aromatic polyamideimide is a polymer having a recurring unit represented by the formula: ##STR47##
 6. A resin composition defined in claim 1 wherein said aromatic polyamideimide is a polymer having a recurring unit represented by the formula: ##STR48## 